| FORTRON ICE 504L is a 40% glass fiber reinforced material that belongs to our new generation of PPS. This new technology allows you to optimize your molding conditions with faster cycle times for complex shapes or process with low mold temperatures.&& |
| Product Description | |
|---|---|
| Supplier | Celanese |
| Generic | PPS |
| Material Status | Commercial: Active |
| Features | Quick molding cycle,V-0 |
| Availabilitys | North America,Europe |
| Technical Data | |||
|---|---|---|---|
| IMPACT | Nominal value | Unit | Test method |
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 10 | kJ/m² | ISO 179/1eA |
| 23℃ | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 53 | kJ/m² | ISO 179/1eU |
| 23℃ | 53 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -30℃ | 10 | kJ/m² | ISO 180-1A |
| 23℃ | 10 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 34 | kJ/m² | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 8.0 MPa, unannealed | 215 | ℃ | ISO 75-2/C |
| 1.8 MPa, unannealed | 270 | ℃ | ISO 75-2/A |
| Glass transition temperature | 90.0 | ℃ | ISO 11357-2 |
| Melting temperature | 280 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| TD | 4.2E-5 | 1/℃ | ISO 11359-2 |
| MD | 2.6E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | 28 | kV/mm | IEC 60243-1 |
| Relative permittivity | |||
| 1 MHz | 4.60 | IEC 60250 | |
| Dissipation factor | |||
| 1 MHz | 6.2E-3 | IEC 60250 | |
| Compared to the leakage tracing index | 125 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.38 mm | V-0 | UL 94 | |
| 1.50 mm | V-0 | UL 94 | |
| Extreme oxygen index | 47 | % | ISO 4589-2 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 14700 | MPa | ISO 527-2/1A/1 |
| tensile strength | |||
| fracture | 195 | MPa | ISO 527-2/1A/5 |
| Tensile strain | |||
| fracture | 1.9 | % | ISO 527-2/1A/5 |
| Bending modulus | |||
| 23℃ | 14500 | MPa | ISO 178 |
| bending strength | 285 | MPa | ISO 178 |
| Rockwell hardness | |||
| M-level | 100 | ISO 2039-2 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.65 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 0.40 to 0.60 | % | ISO 294-4 |
| MD | 0.20 to 0.60 | % | ISO 294-4 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.020 | % | ISO 62 |
| Melt Specific Heat | 1500 | J/kg/℃ | Internal Method |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 130 to 140 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Hopper temperature | 20 to 30 | °C | |
| Barrel rear temperature | 290 to 300 | °C | |
| Barrel middle temperature | 310 to 320 | °C | |
| Barrel front temperature | 330 to 340 | °C | |
| Nozzle temperature | 310 to 330 | °C | |
| Processing (melt) temperature | 330 to 340 | °C | |
| Mold temperature | 90 to 160 | °C | |
| Injection pressure | 50.0 to 100 | MPa | |
| Injection speed | Fast | ||
| Hold pressure | 30.0 to 70.0 | MPa | |
| Back pressure | 0.00 to 3.00 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |