| About |
|---|
| 35% Glass Reinforced, Heat Stabilized, Hydrolysis resistant&& |
| Product Description | |
|---|---|
| Supplier | DSM |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Hydrolysis stability,Heat Stabilized |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.41 | g/cm³ | |
| Shrinkage rate | |||
| TD | 1.0 | % | |
| MD | 0.20 | % | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 5.5 | % | |
| Equilibrium, 23 ℃, 50% RH | 1.5 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 11500 | MPa | |
| tensile strength | |||
| fracture | 210 | MPa | |
| Tensile strain | |||
| fracture | 3.5 | % | |
| Bending modulus | 9400 | MPa | |
| bending strength | 270 | MPa |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 11 | kJ/m² | |
| 23℃ | 14 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| -30℃ | 74 | kJ/m² | |
| 23℃ | 89 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 260 | ℃ | |
| 1.8 MPa, unannealed | 247 | ℃ | |
| Melting temperature | 260 | ℃ | |
| Linear coefficient of thermal expansion | |||
| MD | 2.0E-5 | 1/℃ | |
| TD | 6.0E-5 | 1/℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+14 | ohms·cm | |
| Dielectric strength | 35 | kV/mm | |
| Relative permittivity | |||
| 100 Hz | 4.00 | ||
| 1 MHz | 3.60 | ||
| Dissipation factor | |||
| 100 Hz | 5.0E-3 | ||
| 1 MHz | 0.014 | ||
| Compared to the leakage tracing index | 500 | V |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flammability level | |||
| 0.71 mm | HB | ||
| 1.5 mm | HB |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Barrel rear temperature | 275 to 295 | °C | |
| Barrel middle temperature | 275 to 295 | °C | |
| Barrel front temperature | 275 to 290 | °C | |
| Nozzle temperature | 280 to 290 | °C | |
| Processing (melt) temperature | 290 to 305 | °C | |
| Mold temperature | 50 to 80 | °C | |
| Injection speed | 中等偏快 | ||
| Back pressure | 3.00 to 10.0 | MPa | |
| Screw compression ratio | 2.5:1.0 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |