| About |
|---|
| Kingfa TR-100 is an Acrylonitrile Butadiene Styrene (ABS) material. It is available in Asia Pacific or North America for injection molding. Important attributes of Kingfa TR-100 are: Flame Rated Clarity Typical applications include: Appliances Consumer Goods Electrical/Electronic Applications Tools&& |
| Product Description | |
|---|---|
| Supplier | Kingfa |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | Good Clarity |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.10 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 220℃，10.0kg | 25 | g/10min | ISO 1133 |
| Shrinkage rate | |||
| 23℃ | 0.40 to 0.70 | % | ISO 2577 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 10 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 78.0 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| B120 | 91.0 | ℃ | ISO 306/B120 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | ||
| 3.00 mm | HB |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Transmittance | |||
| 2000 µm | 89.0 | % | ISO 13468 |
| Haze | |||
| 2000 µm | 1.8 | % | ISO 14782 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 113 | ISO 2039-2 | |
| tensile strength | 50.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | 15 | % | ISO 527-2/50 |
| Bending modulus | 2300 | MPa | ISO 178 |
| bending strength | 74.0 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 to 90 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Barrel rear temperature | 180 to 205 | °C | |
| Barrel middle temperature | 205 to 230 | °C | |
| Barrel front temperature | 215 to 240 | °C | |
| Processing (melt) temperature | 210 to 240 | °C | |
| Mold temperature | 30 to 80 | °C | |
| Injection speed | 慢to中等 | ||
| Back pressure | 0.00 to 1.00 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |