| About |
|---|
| SECCO K4912 is a Polypropylene Random Copolymer (PP Random Copolymer) material. It is available in Asia Pacific. Important attributes of SECCO K4912 are: RoHS Compliant Copolymer Typical application of SECCO K4912: Food Contact Applications&& |
| Product Description | |
|---|---|
| Supplier | SECCO |
| Generic | PP copolymer |
| Material Status | Commercial: Active |
| Features | Random copolymer |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 12 | g/10min | ISO 1133 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 6.0 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 74.0 | ℃ | ISO 75-2/B |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Transmittance | |||
| 1000 µm | 87.0 | % | ISO 14782 |
| Haze | |||
| 1000 µm | 11 | % | ISO 14782 |
| Yellowness index | 0 | YI | ASTM E313 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 80 | ISO 2039-2 | |
| tensile strength | ISO 527-2/50 | ||
| yield | 28.0 | MPa | ISO 527-2/50 |
| fracture | 18.0 | MPa | ISO 527-2/50 |
| Bending modulus | 1000 | MPa | ISO 178 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |