| EMERGE™ PC/ABS 7600 是一种阻燃的PC/ABS合金，不含氯或者溴类添加剂。该产品综合了PC树脂优异的物理性能和ABS树脂优异的加工性能，使其具有韧性高、易流动的特点。这种树脂提供了成本与性能之间极佳的平衡。 应用领域： 信息技术设备 消费类电子产品 办公设备和商用设备 零售用设备&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good flexibility,High liquidity,Halogen free,Biocompatible,Flame Characteristics,V-0,5VB |
| Availabilitys | North America,Latin America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.18 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，3.80kg | 19 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.40 to 0.60 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23 ℃, 3.2mm, injection molding | 590 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 77.2 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 87.8 | ℃ | ASTM D648 |
| Vicat Softening Temp | 102 | ℃ | ASTM D1525 3 |
| Ball pressure temperature | 87.2 | ℃ | IEC 60335-1 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.50 mm | V-0 | UL 94 | |
| 2.00 mm | 5VB | UL 94 | |
| Glowing wire flammability index | |||
| 2.0 mm | 950 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | |||
| 2 mm | 825 | ℃ | IEC 60695-2-13 |
| Extreme oxygen index | 31 | % | ASTM D2863 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 3.20 mm, injection molded | 2690 | MPa | ASTM D638 |
| tensile strength | |||
| Fracture, 3.20 mm, injection molded | 44.1 | MPa | ASTM D638 |
| Yield, 3.20 mm, injection molding | 55.2 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 3.20 mm, injection molded | 80 | % | ASTM D638 |
| Yield, 3.20 mm, injection molding | 4.0 | % | ASTM D638 |
| Bending modulus | |||
| 3.20 mm, injection molded | 2830 | MPa | ASTM D790 |
| bending strength | |||
| 3.20 mm, injection molded | 88.9 | MPa | ASTM D790 |
| Rockwell hardness | |||
| R-grade, 3.20 mm | 118 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 79 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Processing (melt) temperature | 216 to 241 | °C | |
| Melt temperature (target) | 221 | °C | |
| Mold temperature | 60 to 71 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |