LNP™ THERMOCOMP™ Compound D151RC

About
LNP* Thermocomp* D151RC (experimental grade name as EXTC8482) is a compound based on Recycle Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: high modulus, good surface, good flatness, good ductility, Non-Brominated u0026amp; Non-Chlorinated Flame Retardant. Post-Consumer Recycling (PCR) polycarbonate content up to 35%.

Product Description
Supplier	SABIC
Generic	Polycarbonate
Material Status	Commercial: Active
Availabilitys	Asia Pacific

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.27	g/cm³	ASTM D792
Melt Flow Rate
300℃，1.20kg	12	g/10min
300℃，2.16kg	24	g/10min
Melt Volume Rate
300℃，1.2 kg	11.0	cm³/10min
300℃，2.16 kg	23.0	cm³/10min
Shrinkage rate
MD：24 hrs	0.30 to 0.50	%
TD：24 hrs	0.30 to 0.50	%
Water absorption rate
23℃，24hr	0.040	%	ISO 62

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus
—	4430	MPa	ASTM D638
—	4380	MPa	ISO 527-1-2
Tensile strength
fracture	82.0	MPa	ASTM D638
fracture	82.0	MPa	ISO 527-2/5
Tensile strain
fracture	3.7	%	ASTM D638
fracture	3.6	%	ISO 527-2/5
Bending modulus
50 mm span	4070	MPa	ASTM D790
—	4180	MPa	ISO 178
Bending stress
—	134	MPa	ISO 178
—	132	MPa	ISO 178
Yield, 50.0 mm span	133	MPa	ASTM D790
Fracture, 50.0 mm span	130	MPa	ASTM D790

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
-30℃	75	J/m	ASTM D256
23℃	140	J/m	ASTM D256
-30℃	7.0	kJ/m²	ISO 180-1A
23℃	13	kJ/m²	ISO 180-1A
Notched impact strength of cantilever beam
23℃	700	J/m	ASTM D4812
23℃	42	kJ/m²	ISO 180/1U
Dart impact equipped with measuring instruments (23 ° C, Total Energy)	21.0	J	ASTM D3763

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed, 3.2 mm	121	℃	ASTM D648
0.45 MPa, unannealed, 4.0 mm, 64 mm span	121	℃	ISO 75-2/Bf
1.8 MPa, unannealed, 3.2 mm	115	℃	ASTM D648
1.8 MPa, unannealed, 4.0 mm, 64 mm span	115	℃	ISO 75-2/Af
Vicat Softening Temp
—	123	℃	ISO 306
—	126	℃	ISO 306/B120
Linear coefficient of thermal expansion
MD：-40~40℃	3.5E-5	1/℃
MD：23~80℃	4.0E-5	1/℃
TD：-40~40℃	6.9E-5	1/℃
TD：23~80℃	8.3E-5	1/℃

Electrical performance	Nominal value	Unit	Test method
Surface resistivity	> 1.0E+16	ohms	ASTM D257
Volume resistivity	> 1.0E+16	ohms·cm	ASTM D257
Dielectric constant
1.10 GHz	3.03
1.9 GHz	3.04
5.00 GHz	3.05
10.0 GHz	3.05
Dissipation factor
1.1 GHz	6.4E-3
1.9 GHz	6.3E-3
5 GHz	6.2E-3
10 GHz	6.4E-3

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant level
0.60 mm	V-0		UL 94

Process Conditions
Injection	Nominal value	Unit	Test method
drying temperature	110	°C
Drying time	3.0 to 6.0	hr
Recommended maximum moisture content	0.020	%
Temperature at the rear of the barrel	260 to 280	°C
Temperature in the middle of the barrel	270 to 290	°C
Front temperature of material barrel	280 to 300	°C
Nozzle temperature	285 to 305	°C
Processing (melt) temperature	285 to 310	°C
Mold temperature	80 to 110	°C
Back pressure	0.100 to 0.300	MPa
Screw speed	50 to 90	rpm

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.