| About |
|---|
| Description High Impact Applications Automotive Parts&& |
| Product Description | |
|---|---|
| Supplier | LG Chemical |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | High impact resistance |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.32 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：23℃，3.2 mm | 0.90 to 1.3 | % | ASTM D955 |
| Water absorption rate | |||
| balance | 1.0 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃，3.2mm | 69 | J/m | ASTM D256 |
| 23℃，3.2mm | 98 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 6.4 mm | 190 | ℃ | ASTM D648 |
| Melting peak temperature | 220 | ℃ | ASTM D3418 |
| Linear coefficient of thermal expansion | |||
| MD | 5.5E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | |||
| 23℃ | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric strength | |||
| 23 ℃，1 mm | 22 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 23 ℃，1 MHz | 4.00 | ASTM D150 | |
| Arc resistance | 185 | sec | ASTM D495 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 113 | ASTM D785 | |
| tensile strength | |||
| Fracture, 3.20 mm | 53.9 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 3.20 mm | 12 | % | ASTM D638 |
| Bending modulus | |||
| 6.40 mm | 2750 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 6.40 mm | 98.1 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 to 100 | °C | |
| Drying time | 4.0 to 5.0 | hr | |
| Barrel rear temperature | 240 to 270 | °C | |
| Barrel middle temperature | 245 to 275 | °C | |
| Barrel front temperature | 245 to 275 | °C | |
| Nozzle temperature | 250 to 280 | °C | |
| Processing (melt) temperature | 250 to 280 | °C | |
| Mold temperature | 60 to 80 | °C | |
| Back pressure | 0.981 to 2.94 | MPa | |
| Screw speed | 60 to 150 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. 0.11 in/min |
| 4. 23°C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |