| About |
|---|
| EMERGE™ PC 8701 advanced resin is an ignition resistant, 10% glass reinforced, polycarbonate resin. This resin contains no bromine, chlorine or phosphate additives. The resin is designed to meet the German norm DIN VDE-0472/Part 815 (1989) on halogens. It is a medium flow PC resin with a mold release system, intended for injection molding applications. Applications: Electrical meter Information Technology Equipment Other structural part&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Halogen free,Flame Characteristics,Moderate liquidity,V-0 |
| Availabilitys | Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.28 | g/cm³ | ISO 1183/B |
| Melt Flow Rate | |||
| 300℃，1.20kg | 8.0 | g/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 0.40 to 0.60 | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 4 mm, injection molded | 3950 | MPa | ISO 527-1-2 |
| 4 mm, injection molded | 4000 | MPa | ISO 527-2/50 |
| tensile strength | ISO 527-2/50 | ||
| Yield, 4 mm, injection molding | 65.0 | MPa | ISO 527-2/50 |
| Fracture, 4 mm, injection molded | 50.0 | MPa | ISO 527-2/50 |
| Tensile strain | ISO 527-2/50 | ||
| Yield, 4 mm, injection molding | 4.0 | % | ISO 527-2/50 |
| Fracture, 4 mm, injection molded | 9.0 | % | ISO 527-2/50 |
| Bending modulus | |||
| 4 mm, injection molded | 3800 | MPa | ISO 178 |
| bending strength | |||
| 4 mm, injection molded | 105 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23 ℃, injection molding | 9.0 | kJ/m² | ISO 180-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 141 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 133 | ℃ | ISO 75-2/A |
| 1.8 MPa, annealed | 139 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| — | 155 | ℃ | ISO 306/A120 |
| B50 | 145 | ℃ | ISO 306 |
| Ball pressure temperature | > 130 | ℃ | IEC 60335-1 |
| Linear coefficient of thermal expansion | |||
| MD：-40~80℃ | 1.5E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume resistivity | |||
| 2 mm | 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric strength | |||
| 2 mm | > 70 | kV/mm | IEC 60243-1 |
| Dielectric constant | IEC 60250 | ||
| 2.00 mm，50 Hz | 3.00 | IEC 60250 | |
| 2.00 mm，1 MHz | 3.10 | IEC 60250 | |
| Dissipation factor | IEC 60250 | ||
| 2 mm，50 Hz | 8.0E-3 | IEC 60250 | |
| 2 mm，1 MHz | 0.016 | IEC 60250 | |
| Compared to the leakage tracing index | |||
| 3.00 mm, solution A | 200 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | V-0 | UL 94 | |
| Igniting temperature of the hot wire | IEC 60695-2-13 | ||
| 1 mm | 960 | ℃ | IEC 60695-2-13 |
| 2 mm | 960 | ℃ | IEC 60695-2-13 |
| 3 mm | 960 | ℃ | IEC 60695-2-13 |
| Extreme oxygen index | 29 | % | ISO 4589-2 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Processing (melt) temperature | 290 to 315 | °C | |
| Mold temperature | 80 to 115 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 3. 4 mm |
| 4. This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |