About
Poly (1, 4-butanediol Succinate) (hereunder PBS) is a kind of fully biodegradable macromolecular polymer that is synthesized from succinic acid and butanediol through a direct process of condensation polymerization. On specific conditions, this material can be finally decomposed safely and innoxiously into simple compounds such as CO2, H2O, etc. PBS has predominant characteristics such as good thermal stability, fine mechanical and processing performance. It can be molding processed in normal plastic fabrication apparatus. Because of its excellent integrated performance, it also can be blended with other fully biodegradable plastic materials to modify the property to satisfy all kinds of manufacturing requirements of plastic products.&&

About

Poly (1, 4-butanediol Succinate) (hereunder PBS) is a kind of fully biodegradable macromolecular polymer that is synthesized from succinic acid and butanediol through a direct process of condensation polymerization. On specific conditions, this material can be finally decomposed safely and innoxiously into simple compounds such as CO2, H2O, etc. PBS has predominant characteristics such as good thermal stability, fine mechanical and processing performance. It can be molding processed in normal plastic fabrication apparatus. Because of its excellent integrated performance, it also can be blended with other fully biodegradable plastic materials to modify the property to satisfy all kinds of manufacturing requirements of plastic products.&&

Product Description
Supplier	Xinfu
Generic	PBS
Material Status	Commercial: Active
Features	Excellent Processability,Biodegradable,Heat Stabilized
Availabilitys	Asia Pacific
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.15 to 1.25	g/cm³
Melt Flow Rate	> 15	g/10min
Ash Content	< 0.50	%

MECHANICAL	Nominal value	Unit
tensile strength
fracture	> 20.0	MPa
Tensile strain
fracture	> 200	%
Bending modulus	> 300	MPa
bending strength	> 20.0	MPa

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch	> 4.0	kJ/m²

THERMAL	Nominal value	Unit
Vicat Softening Temp	> 101	℃
Melting temperature	43.3 to 48.9	℃
Hot deformation temperature	> 80	℃

Supplementary information	Nominal value	Unit	Test method
Loss on Drying	< 0.50	%

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.