| About |
|---|
| Ultramid A3HG2 is a 10% glass fiber reinforced injection molding PA66 grade. Applications Typical applications include machinery components and housings of medium stiffness, as well as electrically insulating parts.&& |
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Grease resistance |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ASTM D792 |
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 275℃，5 kg | 80.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.80 | % | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 7.0 | % | ISO 62 |
| saturated | 7.0 | % | ASTM D570 |
| Equilibrium, 23 ℃, 50% RH | 2.1 | % | ISO 62 |
| Balance, 50% RH | 2.1 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 4600 | MPa | ISO 527-2 |
| tensile strength | |||
| Fracture, 23 ℃ | 100 | MPa | ISO 527-2 |
| Fracture, 23 ℃ | 100 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃ | 3.0 | % | ASTM D638 |
| Fracture, 23 ℃ | 3.0 | % | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 4480 | MPa | ASTM D790 |
| 23℃ | 4480 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 7.0 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | |||
| 23℃ | 30 | kJ/m² | ISO 179 |
| Impact strength of cantilever beam notch | |||
| 23℃ | 53 | J/m | ASTM D256 |
| 23℃ | 5.5 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 210 | ℃ | ISO 75-2/A |
| 1.8 MPa, unannealed | 210 | ℃ | ASTM D648 |
| Melting peak temperature | 260 | ℃ | ASTM D3418 |
| Melting temperature | |||
| DSC | 260 | ℃ | ISO 3146 |
| Linear coefficient of thermal expansion | |||
| TD | 7.5E-5 | 1/℃ | |
| MD | 3.3E-5 | 1/℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+13 | ohms·cm | IEC 60093 |
| 1.50 mm | 1.0E+13 | ohms·cm | ASTM D257 |
| Dielectric constant | |||
| 1 MHz | 3.50 | IEC 60250 | |
| Dissipation factor | |||
| 1 MHz | 0.014 | IEC 60250 | |
| Compared to the leakage tracing index | 550 | V | IEC 60112 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.15 | % | |
| Processing (melt) temperature | 280 to 305 | °C | |
| Mold temperature | 80 to 90 | °C | |
| Injection pressure | 3.50 to 12.5 | MPa | |
| Injection speed | Fast | ||
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |