| About |
|---|
| Vydyne ECO315J BK0707 is a non-halogenated, unfilled, flame-retardant PA66/6 copolymer with excellent toughness and ductility. It is stabilized to provide heat stability up to 125°C for 1,000 hours in a dry environment. ECO315J BK0707 is also lubricated for machine feed and easy mold release and has an Underwriters Laboratories UL 94 flammability classification of V-0 at 0.4 mm (0.016″) thick.&& |
| Product Description | |
|---|---|
| Supplier | Ascend |
| Generic | PA66/6 |
| Material Status | Commercial: Active |
| Features | Good flexibility,Ductility,Halogen free,Good stripping performance,Flame Characteristics,Lubricating,Good Tensile Strength,Low density,Good tear strength,V-0 |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.16 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD：23℃，2.0 mm | 1.4 | % | ISO 294-4 |
| MD：23℃，2.0 mm | 1.2 | % | ISO 294-4 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 2.3 | % | ISO 62 |
| 23℃，24hr | 0.80 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 5000 | MPa | ISO 527-2 |
| tensile strength | |||
| Yield, 23 ℃ | 75.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 25 | % | ISO 527-2 |
| Yield, 23 ℃ | 5.5 | % | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 3200 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 92.0 | MPa | ISO 178 |
| Poisson’s ratio | 0.40 | ISO 527-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 5.4 | kJ/m² | ISO 179/1eA |
| 23℃ | 5.4 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | No Break | ISO 179/1eU | |
| 23℃ | No Break | ISO 179/1eU | |
| Impact strength of cantilever beam notch | |||
| 23℃ | 6.0 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 65.0 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 225 | ℃ | ISO 75-2/B |
| Melting temperature | 244 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| TD：23~55℃，2 mm | 1.1E-4 | 1/℃ | ISO 11359-2 |
| MD：23~55℃，2 mm | 1.1E-4 | 1/℃ | ISO 11359-2 |
| 0.40 mm | 130 | ℃ | UL 746 |
| 0.75 mm | 130 | ℃ | UL 746 |
| 1.5 mm | 130 | ℃ | UL 746 |
| 3.0 mm | 130 | ℃ | UL 746 |
| Relative temperature index | |||
| Electrical performance | UL 746 | ||
| Strength mechanical performance | UL 746 | ||
| Impact mechanical performance | UL 746 | ||
| 0.40 mm | 65.0 | ℃ | UL 746 |
| 0.75 mm | 65.0 | ℃ | UL 746 |
| 1.5 mm | 85.0 | ℃ | UL 746 |
| 3.0 mm | 85.0 | ℃ | UL 746 |
| 0.40 mm | 100 | ℃ | UL 746 |
| 0.75 mm | 100 | ℃ | UL 746 |
| 1.5 mm | 100 | ℃ | UL 746 |
| 3.0 mm | 110 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | |||
| 0.75 mm | 1.0E+11 | ohms·cm | IEC 60093 |
| Dielectric strength | |||
| 1 mm | 13 | kV/mm | IEC 60243 |
| Arc resistance | |||
| 3.0 mm | PLC 5 | ASTM D495 | |
| Compared to the leakage tracing index | |||
| 3.00 mm | 600 | V | IEC 60112 |
| High Arc Burning Index (HAI) | UL 746 | ||
| 0.40 mm | PLC 0 | UL 746 | |
| 0.75 mm | PLC 0 | UL 746 | |
| 1.5 mm | PLC 0 | UL 746 | |
| 3.0 mm | PLC 0 | UL 746 | |
| High voltage arc marking rate | |||
| HVTR | PLC 1 | UL 746 | |
| Hot wire ignition | |||
| HWI | UL 746 | ||
| 0.40 mm | PLC 4 | UL 746 | |
| 0.75 mm | PLC 4 | UL 746 | |
| 1.5 mm | PLC 4 | UL 746 | |
| 3.0 mm | PLC 3 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.40 mm | V-0 | UL 94 | |
| 0.75 mm | V-0 | UL 94 | |
| 1.50 mm | V-0 | UL 94 | |
| 3.00 mm | V-0 | UL 94 | |
| Glowing wire flammability index | IEC 60695-2-12 | ||
| 0.40 mm | 960 | ℃ | IEC 60695-2-12 |
| 0.75 mm | 960 | ℃ | IEC 60695-2-12 |
| 1.5 mm | 960 | ℃ | IEC 60695-2-12 |
| 3.0 mm | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | IEC 60695-2-13 | ||
| 0.4 mm | 875 | ℃ | IEC 60695-2-13 |
| 0.75 mm | 875 | ℃ | IEC 60695-2-13 |
| 1.5 mm | 775 | ℃ | IEC 60695-2-13 |
| 3 mm | 725 | ℃ | IEC 60695-2-13 |
| Extreme oxygen index | 29 | % | ISO 4589-2 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 4.0 | hr | |
| Proposed maximum recycled material ratio | 50 | % | |
| Barrel rear temperature | 240 to 270 | °C | |
| Barrel middle temperature | 240 to 270 | °C | |
| Barrel front temperature | 240 to 270 | °C | |
| Nozzle temperature | 240 to 270 | °C | |
| Processing (melt) temperature | 250 to 270 | °C | |
| Mold temperature | 65 to 95 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |