| Injection molding grade. For molded products with superior balance of high-level impact strength and rigidity, maximum transparency, and good surface appearance. It is supplied in pellet form. Food containers, cosmetics caps, pencil cases and other stationery goods, toys, swim goggle and other cases, consumer goods&& |
| Product Description | |
|---|---|
| Supplier | Asahi Kasei |
| Generic | SBS |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Clarity,Good surface appearance,High impact resistance,Copolymer |
| Availabilitys | Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.02 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD | 0.20-0.80 | % | ISO 294-4 |
| Water absorption rate | |||
| 23℃，24hr | <0.10 | % | ISO 62 |
| Melt Flow Rate | |||
| 200℃，5.0kg | 10 | g/10min | ISO 1133 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Transmittance | |||
| 2000 μm | 90 | % | ISO 13468-2 |
| Haze | 0.50 | % | ISO 14782 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed | 63 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | |||
| A50 | 91 | ℃ | ISO 306/A50 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 16 | kJ/m² | ISO 179/1eU |
| Charpy Notched Impact Strength | |||
| 23℃ | 1.3 | kJ/m² | ISO 179/1eA |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 75 | ISO 868 | |
| Rockwell hardness | 88 | R 级 | ISO 2039-2 |
| tensile strength | |||
| 23℃ | 30 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 15 | % | ISO 527-2 |
| bending strength | |||
| 23℃ | 50 | MPa | ISO 178 |
| Bending modulus | |||
| 23℃ | 1550 | MPa | ISO 178 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |