| 改性PVC，UL94 V-0@1.5mm-3.0mm, 5VA@2.0mm ，机械强度好，良好的耐热老化性，良好的表面，良好的加工性能 |
| Product Description | |
|---|---|
| Supplier | Kingfa |
| Generic | PVC, not specified |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,Good heat aging resistance |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Shore hardness | |||
| 5 seconds | 75 | D 级 | ASTM D2240 |
| tensile strength | |||
| 50 mm/min | 43 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 50 mm/min | 10 | % | ASTM D638 |
| bending strength | |||
| 2 mm/min | 63 | MPa | ASTM D790 |
| Bending modulus | |||
| 2 mm/mim | 2200 | MPa | ASTM D790 |
| Rockwell hardness | |||
| R-level | 105 | ASTM D785 | |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa | 72 | ℃ | ASTM D648 |
| Vicat Softening Temp | |||
| B50 | 76 | ℃ | ASTM D1525 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 10^14-10^16 | ohms·cm | IEC 60093 |
| other | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.80 mm | |||
| 1.5mm | V-0 | Class | UL 94 |
| 3.0mm | V-0 | Class | UL 94 |
| 2.0mm | 5VA | Class | UL 94 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 500 | kJ/m² | ASTM D256 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shrinkage rate | |||
| 23℃ | 0.2-0.6 | % | ASTM D955 |
| Density | 1.24 | g/cm³ | ASTM D792 |
| Process Conditions | |||
|---|---|---|---|
| injection molding | Nominal value | Unit | Test method |
| Temperature of the rear section of the barrel | 180-210 | °C | |
| Temperature in the middle section of the barrel | 140-160 | °C | |
| Temperature of the front section of the material barrel | 150-170 | °C | |
| Core temperature | 150-180 | °C | |
| Mold temperature | 20-60 | °C | |
| Upper limit of processing temperature | 190 | °C | |
| Pre-drying | 60-70°C，2-4hrs | ||
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |