TOPAS® 7010F-600

About
TOPAS® 7010F-600 Product Description TOPAS 7010F-600 is a robust film extrusion grade designed for blending with polyethylene (PE). It is a moderate clarity amorphous resin with high stiffness, moisture barrier, chemical resistance, thermoformability and purity for food and general purpose applications. It is used in blends in both cast and blown processes, and in monolayer and multilayer products. Leading film applications include twist wrap, forming webs, protective packaging, shrink films and labels, and easy tear packaging. Industrial uses include formed PE and PP sheet products. For property enhancement at elevated temperatures, higher glass transition temperature (Tg) grades of TOPAS are recommended. Selected Applications Forming films (header bags, etc.) Protective packaging Shrink films and labels Twist films Decorative sheet Food packaging Food contact Leading Attributes Clarity, forming, barrier, purity, halogen-free Stiffness for downgauging, improved forming High shrink, low stress, gloss, toughness Outstanding deadfold, clean cutting Stiffness, chemical resistance, forming, even draw Not manufactured with BPA, phthalates, or halogens Broad regulatory approval Related Grades for Packaging and Film Extrusion TOPAS 8007F-04 – ultimate clarity extrusion grade TOPAS 8007F-600 – robust clarity extrusion grade especially for PE blends&&TOPAS® 7010F-600 TOPAS® 7010F-600 is a Cyclic Olefin Copolymer (COC) product. It is available in Africa & Middle East, Asia Pacific, or Latin America. Typical application: Film. Characteristics include: Copolymer Good Processability Heat Resistant&&

About

TOPAS® 7010F-600 Product Description TOPAS 7010F-600 is a robust film extrusion grade designed for blending with polyethylene (PE). It is a moderate clarity amorphous resin with high stiffness, moisture barrier, chemical resistance, thermoformability and purity for food and general purpose applications. It is used in blends in both cast and blown processes, and in monolayer and multilayer products. Leading film applications include twist wrap, forming webs, protective packaging, shrink films and labels, and easy tear packaging. Industrial uses include formed PE and PP sheet products. For property enhancement at elevated temperatures, higher glass transition temperature (Tg) grades of TOPAS are recommended. Selected Applications Forming films (header bags, etc.) Protective packaging Shrink films and labels Twist films Decorative sheet Food packaging Food contact Leading Attributes Clarity, forming, barrier, purity, halogen-free Stiffness for downgauging, improved forming High shrink, low stress, gloss, toughness Outstanding deadfold, clean cutting Stiffness, chemical resistance, forming, even draw Not manufactured with BPA, phthalates, or halogens Broad regulatory approval Related Grades for Packaging and Film Extrusion TOPAS 8007F-04 – ultimate clarity extrusion grade TOPAS 8007F-600 – robust clarity extrusion grade especially for PE blends&&TOPAS® 7010F-600 TOPAS® 7010F-600 is a Cyclic Olefin Copolymer (COC) product. It is available in Africa & Middle East, Asia Pacific, or Latin America. Typical application: Film. Characteristics include: Copolymer Good Processability Heat Resistant&&

Product Description
Supplier	Polyplastics
Generic	COC
Material Status	Commercial: Active
Features	Good Rigidity,Good flexibility,High purity,Good surface appearance,Halogen free,Food contact compliance,Moisture resistance,No BPA,Copolymer,Solvent resistance,High shrinkage,Amorphous
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.02	g/cm³	ISO 1183
Melt Flow Rate			ISO 1133
190℃，2.16kg	1.8	g/10min	ISO 1133
230℃，2.16kg	10	g/10min	ISO 1133
Melt Volume Rate			ISO 1133
190℃，2.16 kg	2.00	cm³/10min	ISO 1133
230℃，2.16 kg	11.0	cm³/10min	ISO 1133
Water absorption rate
Saturation, 23 ℃	0.010	%	ISO 62

film	Nominal value	Unit	Test method
film thickness
test	70	µm
Tensile modulus			ISO 527-3/1
MD, 70 µ m, cast thin film	2100	MPa	ISO 527-3/1
TD, 70 µ m, cast thin film	1700	MPa	ISO 527-3/1
tensile strength			ISO 527-3/50
MD, fracture, 70 µ m, blow molded film	55.0	MPa	ISO 527-3/50
TD, fracture, 70 µ m, blow molded film	50.0	MPa	ISO 527-3/50
Tensile strain			ISO 527-3/50
MD, fracture, 70 µ m, cast thin film	3.4	%	ISO 527-3/50
TD, fracture, 70 µ m, cast thin film	3.4	%	ISO 527-3/50
Oxygen permeability
23 ℃, 70 µ m, extruded film, 50% RH	25	cm³·mm/m²/atm/24 hr	ASTM D3985
Water vapor transmittance
70 µ m, 23 ℃, cast film, 85% RH	0.094	g·mm/m²/atm/24 hr	ASTM F1249

THERMAL	Nominal value	Unit	Test method
Glass transition temperature	78.0	℃	ISO 11357-2

optical performance	Nominal value	Unit	Test method
gloss
60 °, 70.0 µ m, cast thin film	> 100		ISO 2813
Haze
70.0 µ m, cast thin film	> 2.0	%	ISO 14782

Process Conditions
Extrusion	Nominal value	Unit	Test method
Extruder feed section	20 to 70	°C
Barrel 1 zone temperature	210 to 230	°C
Barrel 2 zone temperature	220 to 240	°C
Barrel 3 zone temperature	220 to 240	°C
Barrel 4 zone temperature	220 to 240	°C
Nozzle temperature	220 to 240	°C

Notes
1. Typical properties: these are not to be construed as specifications.
2. 90% RH
3. 10°C/min
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.