| Thermal conductive material, Flame Retardant, Heat Stabilized, 20% Glass Reinforced&& |
| Product Description | |
|---|---|
| Supplier | DSM |
| Generic | PA 46 |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,Thermal conductivity,Heat Stabilized |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.87 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| TD | 0.60 | % | |
| MD | 0.25 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 14000 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 115 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 1.6 | % | ISO 527-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 7.5 | kJ/m² | |
| 23℃ | 8.0 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| -30℃ | 24 | kJ/m² | |
| 23℃ | 24 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 214 | ℃ | ISO 75-2/A |
| Melting temperature | 290 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| MD | 2.1E-5 | 1/℃ | |
| TD | 2.5E-5 | 1/℃ | |
| Thermal conductivity coefficient | |||
| — | 0.90 | W/m/K | |
| — | 2.1 | W/m/K |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | 300 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flammability level | |||
| 0.8 mm | V-0 | IEC 60695-11-10, -20 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 2.0 | hr | |
| Barrel rear temperature | 280 to 320 | °C | |
| Barrel middle temperature | 300 to 320 | °C | |
| Barrel front temperature | 300 to 320 | °C | |
| Nozzle temperature | 305 to 335 | °C | |
| Processing (melt) temperature | 305 to 325 | °C | |
| Mold temperature | 80 to 120 | °C | |
| Injection speed | 中等偏快 | ||
| Back pressure | 2.00 to 10.0 | MPa | |
| Screw compression ratio | 2.5:1.0 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 3. Through Plane |
| 4. In Plane |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |