| About |
|---|
| Product Description | |
|---|---|
| Supplier | Shinkong |
| Generic | TPEE |
| Material Status | Commercial: Active |
| Features | HB |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.19 | g/cm³ | ISO 1183 |
| Water absorption rate | 0.5 | % | ISO 62 |
| Shrinkage rate | ISO 2944 | ||
| TD | 1.5 | % | ISO 2944 |
| MD | 1.5 | % | ISO 2944 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | >24 | MPa | ISO 527-2/1A |
| yield | 14 | MPa | ISO 527-2/1A |
| Tensile modulus | 160 | MPa | ISO 527-2/1A |
| Tensile strain | |||
| fracture | 415 | % | ASTM D638 |
| Bending modulus | 175 | MPa | ISO 178 |
| bending strength | 12 | MPa | ISO 178 |
| Shaw hardness | |||
| D-level | 55 | ISO 868 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 无断裂 | KJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| melting point | |||
| 201 | ℃ | DSC | |
| Hot deformation temperature | ISO 75/Bf | ||
| 1.8 Mpa | 83 | ℃ | ISO 75/Bf |
| 0.45 Mpa | – | ℃ | ISO 75/Bf |
| Melt index | |||
| 230°C/2.16Kg | 17 | g/10min | ISO 1133 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1E+16 | Ω-CM | IEC 60093 |
| Dielectric strength | 15 | KV/mm | IEC 60243-1 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |