| About |
|---|
| POE C0570 is an ethylene octene copolymer produced by solution polymerization using metallocene catalyst. This product is available as free flowing pellets. |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polyolefin Elastomer |
| Material Status | Commercial: Active |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.868 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.50 | g/10min | ASTM D1238 |
| 190℃，2.16kg | 0.5 | g/10min | ASTM D1238 |
| 230℃，2.16kg | 0.9 | g/10min | ASTM D1238 |
| Mooney viscosity | |||
| ML 1+4，121℃ | 36 | MU | ASTM D1646 |
| ML 1+4，121℃ | 36 | MU | ASTM D1646 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ASTM D2240 | ||
| hardness | |||
| 74 | ASTM D2240 | ||
| 23 | ASTM D2240 |
| Film properties | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile property | |||
| fracture | 10.3 | MPa | ASTM D638 |
| Tensile strain | 800 | % | ASTM D638 |
| 100% modulus | 3.1 | MPa | ASTM D638 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting peak temperature | 59 | °C | SABIC method |
| Glass transition temperature | -54 | °C | SABIC method |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |