| About |
|---|
| TB51S is a high crystalline polypropylene offering superior flexural modulus, surface hardness and tensile strength. TB51S is also effectively used to reduce weights in manufactured products.&& |
| Product Description | |
|---|---|
| Supplier | HANWHA |
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Excellent Processability,High impact resistance,Good Hardness,Crystal,High Heat Resistance,Good Tensile Strength,Antistatic property,High scratch resistance |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.980 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 10 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 1.2 to 1.6 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃ | 34 | J/m | |
| 23℃ | 59 | J/m |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 130 | ℃ | ASTM D648 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 105 | ASTM D785 | |
| tensile strength | ASTM D638 | ||
| yield | 34.3 | MPa | |
| fracture | 27.5 | MPa | |
| Tensile strain | |||
| fracture | 15 | % | ASTM D638 |
| Bending modulus | 2350 | MPa | ASTM D790 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |