| About |
|---|
| Amodel® AT-1002 HS is a neat, toughened, heat stabilized polyphthalamide (PPA) resin that offers superior retention of properties after humid thermal aging; high impact at low temperature and better mechanical properties than many unreinforced thermoplastic polyester and nylon resins. This material was specifically designed for automotive electrical/electronic applications such as connectors, sockets and sensors. Natural: AT-1002 HS NT&& |
| Product Description | |
|---|---|
| Supplier | Solvay |
| Generic | PPA |
| Material Status | Commercial: Active |
| Features | Low warping,High impact resistance,Ductility,Lubricating,Solvent resistance,low-temperature impact resistance,Heat Stabilized,HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.13 | g/cm³ | ISO 1183/A |
| Shrinkage rate | |||
| TD | 2.1 | % | ASTM D955 |
| MD | 2.0 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr | 0.50 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2760 | MPa | ASTM D638 |
| Tensile modulus | ISO 527-2 | ||
| 23℃ | 2760 | MPa | ISO 527-2 |
| 100℃ | 2100 | MPa | ISO 527-2 |
| tensile strength | 83.4 | MPa | ASTM D638 |
| Fracture, 23 ℃ | 68.3 | MPa | ISO 527-2 |
| tensile strength | ISO 527-2 | ||
| Yield, 23 ℃ | 75.2 | MPa | ISO 527-2 |
| Yield, 100 ℃ | 38.6 | MPa | ISO 527-2 |
| Tensile strain | ISO 527-2 | ||
| Fracture, 23 ℃ | 15 | % | ISO 527-2 |
| fracture | 80 | % | ASTM D638 |
| Yield, 23 ℃ | 5.0 | % | ISO 527-2 |
| Yield, 100 ℃ | 3.7 | % | ISO 527-2 |
| Bending modulus | 2210 | MPa | ASTM D790 |
| Bending modulus | ISO 178 | ||
| 23℃ | 2280 | MPa | ISO 178 |
| 100℃ | 1720 | MPa | ISO 178 |
| bending strength | 103 | MPa | ASTM D790 |
| bending strength | ISO 178 | ||
| 23℃ | 79.3 | MPa | ISO 178 |
| 100℃ | 49.6 | MPa | ISO 178 |
| shear strength | 64.1 | MPa | ASTM D732 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 13 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | No Break | ISO 179/1eU | |
| Impact strength of cantilever beam notch | 140 | J/m | ASTM D256 |
| 23℃ | 13 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | No Break | ISO 180/1U | |
| Dart impact equipped with measuring instruments | |||
| Total Energy | 54.2 | J | ASTM D3763 |
| Penetration Impact | 4448 | N | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed | 121 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 118 | ℃ | ISO 75-2/Af |
| 0.45 MPa, annealed | 163 | ℃ | ASTM D648 |
| Melting peak temperature | 315 | ℃ | ASTM D3418 |
| Melting temperature | 315 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| TD | ASTM E831 | ||
| MD | ASTM E831 | ||
| 0 to 100 ℃ | 7.8E-5 | cm/cm/℃ | ASTM E831 |
| 100 to 200 ℃ | 1.3E-4 | cm/cm/℃ | ASTM E831 |
| 0 to 100 ℃ | 9.3E-5 | cm/cm/℃ | ASTM E831 |
| 100 to 200 ℃ | 1.4E-4 | cm/cm/℃ | ASTM E831 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 8.0E+13 | ohms | ASTM D257 |
| Volume resistivity | 1.2E+16 | ohms·cm | ASTM D257 |
| Dielectric strength | 17 | kV/mm | ASTM D149 |
| Dielectric constant | ASTM D150 | ||
| 60 Hz | 3.30 | ASTM D150 | |
| 1 MHz | 3.30 | ASTM D150 | |
| Dissipation factor | ASTM D150 | ||
| 60 Hz | 4.0E-3 | ASTM D150 | |
| 1 MHz | 0.016 | ASTM D150 | |
| Compared to the leakage tracing index | > 600 | V | ASTM D3638 |
| High voltage arc marking rate | |||
| HVTR | 12.0 | mm/min | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 110 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.060 | % | |
| Barrel rear temperature | 304 | °C | |
| Barrel front temperature | 324 | °C | |
| Processing (melt) temperature | 321 to 329 | °C | |
| Mold temperature | < 90 | °C | |
| Screw speed | 100 to 200 | rpm | |
| Screw compression ratio | 2.5:1.0 | ||
| Notes |
|---|
| 1. Approval listed in Ford MATS system to this fuel performance specifcation, as well as to Ford WSS-M98P14-A7. |
| 2. Typical properties: these are not to be construed as specifications. |
| 3. Type IV |
| 4. Maximum Load |
| 5. This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |