| Description Flame Retardant, Impact Modified, Dimensional Stability Application E&E(Switch)&& |
| Product Description | |
|---|---|
| Supplier | LG Chemical |
| Generic | PBT Alloy |
| Material Status | Commercial: Active |
| Features | High impact resistance,Good Dimensional Stability,High elastic,Flame Characteristics,V-0 |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.40 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 250℃，3.80kg | 6.0 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.40 to 0.90 | % | ASTM D955 |
| Water absorption rate | |||
| 23℃，24hr | 0.080 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Fracture, 3.20 mm | 55.9 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 3.20 mm | 3.0 | % | ASTM D638 |
| Bending modulus | |||
| 3.20 mm | 3140 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 3.20 mm | 85.3 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，6.4mm | 59 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.4 mm | 110 | ℃ | ASTM D648 |
| Melting peak temperature | 223 | ℃ | ASTM D3418 |
| Relative temperature index | |||
| Electrical performance | 60.0 | ℃ | UL 746 |
| Strength mechanical performance | 60.0 | ℃ | UL 746 |
| Impact mechanical performance | 60.0 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric strength | |||
| 1 mm | 26 | kV/mm | ASTM D149 |
| Arc resistance | PLC 6 | ASTM D495 | |
| Compared to the leakage tracing index | PLC 3 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.50 mm | V-0 | UL 94 | |
| 3.00 mm | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 100 | °C | |
| Drying time | 4.0 to 5.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Barrel rear temperature | 225 to 235 | °C | |
| Barrel middle temperature | 230 to 245 | °C | |
| Barrel front temperature | 240 to 250 | °C | |
| Nozzle temperature | 240 to 250 | °C | |
| Processing (melt) temperature | 240 to 250 | °C | |
| Mold temperature | 40 to 80 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. 0.051 in/min |
| 4. Solution A |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |