| About |
|---|
| PLEXIGLAS® Resist AG 100 is an amorphous thermoplastic molding compound, based on impact-modified polymethyl methacrylate (PMMA). Properties PLEXIGLAS® molding compounds have the following typical properties: high weather resistance excellent transmission and clarity brilliant appearance low weight – half the weight of glass 100% recyclable – best life cycle assessment as compared with glass and PC pleasant feel and sound of molded parts PLEXIGLAS® Resist AG 100 is characterized by the following additional properties: highest breaking strength and impact strength (30 times higher breaking strength than glass) improved resistance to stress cracking balanced property profile clear reduction of reversible haze at very high and low temperatures increased heat deflection temperature under load AMECA listing, CAMPUS and moldflow data available&& |
| Product Description | |
|---|---|
| Supplier | ROHM |
| Generic | PMMA |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Good Clarity,High impact resistance,Renewable resources,Amorphous |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.16 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 230℃，3.8 kg | 1.10 | cm³/10min | |
| 260℃，3.8 kg | 7.70 | cm³/10min | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 1.5 | % | |
| Equilibrium, 23 ℃, 50% RH | 0.50 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2200 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 55.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 5.0 | % | ISO 527-2/50 |
| Nominal tensile fracture strain | 45 | % | ISO 527-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 120 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 105 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 100 | ℃ | ISO 75-2/A |
| Glass transition temperature | 112 | ℃ | ISO 11357-2 |
| Vicat Softening Temp | |||
| B50 | 105 | ℃ | ISO 306 |
| Linear coefficient of thermal expansion | |||
| MD：0~50℃ | 1.1E-4 | 1/℃ | ISO 11359-2 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | HB | IEC 707 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Refractive index | 1.490 | ISO 489 | |
| Transmittance | 91.0 | % | ISO 13468-2 |
| Haze | 0.70 | % | ASTM D1003 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 70 to 80 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Processing (melt) temperature | 235 to 270 | °C | |
| Mold temperature | 60 to 80 | °C | |
| Drying temperature | 70 to 80 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Melt temperature | 235 to 270 | °C | |
| Nozzle temperature | 240 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. D65 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |