Durethan® BKV 20 FN01 000000

About
Durethan® BKV 20 FN01 000000 (干燥 ) PA 6, 18 % glass fibers, injection molding, halogen free flame retardant&&Durethan® BKV 20 FN01 000000 PA 6, 18 % glass fibers, injection molding, halogen free flame retardant&&

Product Description
Supplier	LANXESS
Generic	PA6
Material Status	Commercial: Active
Features	Halogen free,Flame Characteristics,V-0,5VA
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.34	g/cm³	ISO 1183
Melt Volume Rate
260℃，5 kg	37.0	cm³/10min	ISO 1133
Shrinkage rate			ISO 294-4
TD：260℃，2.0 mm	0.60	%	ISO 294-4
TD：120℃，2.0 mm，2 hrs	0.20	%	ISO 294-4
MD：260℃，2.0 mm	0.30	%	ISO 294-4
MD：120℃，2.0 mm，2 hrs	0.10	%	ISO 294-4
Water absorption rate
Saturation, 23 ℃	5.3	%	ISO 62
Equilibrium, 23 ℃, 50% RH	1.6	%	ISO 62

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus
23℃	7960	MPa	ISO 527-1-2
tensile strength
Fracture, 23 ℃	110	MPa	ISO 527-2/5
Tensile strain
Fracture, 23 ℃	3.0	%	ISO 527-2/5
Bending modulus
23℃	7200	MPa	ISO 178-A
bending strength
3.50% strain	—	MPa	ISO 178-A
23℃	170	MPa	ISO 178
Bending strain	3.2	%

IMPACT	Nominal value	Unit	Test method
Charpy Unnotch Impact strength
23℃	50	kJ/m²	ISO 179/1eU
Impact strength of cantilever beam notch
23℃	< 10	kJ/m²	ISO 180-1A
Notched impact strength of cantilever beam
23℃	40	kJ/m²	ISO 180/1U

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	200	℃	ISO 75-2/A
0.45 MPa, unannealed	218	℃	ISO 75-2/B
Vicat Softening Temp
B120	205	℃	ISO 306/B120
Melting temperature	222	℃	ISO 11357-3
Linear coefficient of thermal expansion
TD：23~55℃	9.0E-5	1/℃	ISO 11359-2
MD：23~55℃	3.0E-5	1/℃	ISO 11359-2

Electrical performance	Nominal value	Unit	Test method
Surface resistivity	8.6E+15	ohms	IEC 60093
Volume resistivity
23℃	5.3E+17	ohms·cm	IEC 60093
Compared to the leakage tracing index	PLC 0		UL 746

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant level			UL 94
0.75 mm	V-0		UL 94
1.50 mm	V-0		UL 94
3.00 mm	5VA		UL 94
Glowing wire flammability index			IEC 60695-2-12
0.80 mm	960	℃	IEC 60695-2-12
1.5 mm	960	℃	IEC 60695-2-12
3.0 mm	960	℃	IEC 60695-2-12
Igniting temperature of the hot wire			IEC 60695-2-13
0.75 mm	750	℃	IEC 60695-2-13
1.5 mm	750	℃	IEC 60695-2-13
3 mm	750	℃	IEC 60695-2-13
Extreme oxygen index	34	%	ISO 4589-2

Supplementary information	Nominal value	Unit	Test method
ISO Shortname	PA 6, GFHR, 12-080, GF18; ISO 1043-PA GF FR (30+40+72)		ISO 1874

Process Conditions
injection	Nominal value	Unit	Test method
Drying Temperature – Dry Air Dryer	80	°C
Drying Time – Dry Air Dryer	2.0 to 6.0	hr
Processing (melt) temperature	250 to 270	°C
Mold temperature	80	°C
Residual Moisture Content	0.030 to 0.070	%

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.