| About |
|---|
| Elastollan® 1185AW is a polyether-based thermoplastic polyurethane (TPU) containing a plasticizer. It is specifically formulated for wire and cable, film and sheet, and extruded profile applications. It contains a non-halogenated flame retardant and is rated UL-94 V-2 in vertical flame test for wall thicknesses of 0.75, 1.5 and 3.0 mm. It also passes FAR 25.853 (A) flame test. It exhibits excellent abrasion resistance, toughness, transparency, very good low temperature flexibility, hydrolytic stability and fungus resistance. It has excellent damping characteristics and outstanding resistance to tear propagation. Elastollan® 1185A is supplied uncolored in pellet form.&& |
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | TPU-醚 |
| Material Status | Commercial: Active |
| Features | Good flexibility,Hydrolysis stability,Antimicrobial properties,Low temperature toughness,Good tear strength,Good wear resistance,V-2 |
| Availabilitys | North America |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.16 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，3.80kg | 5.0 to 25 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 85 | ASTM D2240 | |
| Tensile modulus | |||
| injection molding | 19.3 | MPa | ASTM D412 |
| Bending modulus | |||
| injection molding | 20.7 | MPa | ASTM D790 |
| Taber abraser | 35.0 | mg | ASTM D1044 |
| Abrasion（DIN） | 30 | mm³ | DIN 53516 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 34.5 | MPa | ASTM D412 |
| 300% strain | 24.1 | MPa | ASTM D412 |
| 100% strain | 9.65 | MPa | ASTM D412 |
| Tensile strain | |||
| fracture | 560 | % | ASTM D412 |
| tear strength | 110 | kN/m | ASTM D624 |
| Compression deformation | ASTM D395B | ||
| 23℃，22 hr | 25 | % | ASTM D395B |
| 70℃，22 hr | 45 | % | ASTM D395B |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass transition temperature | -47.0 | ℃ | Internal Method |
| Vicat Softening Temp | 100 | ℃ | ASTM D1525 |
| Softening temperature | |||
| DMA | 70 | ℃ | Internal Method |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.75 mm | V-2 | UL 94 | |
| 1.50 mm | V-2 | UL 94 | |
| 3.00 mm | V-2 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 100 to 110 | °C | |
| Drying time | 2.0 to 3.0 | hr | |
| Recommended maximum moisture content | 0.030 | % | |
| Barrel rear temperature | 190 to 220 | °C | |
| Barrel middle temperature | 190 to 220 | °C | |
| Barrel front temperature | 190 to 220 | °C | |
| Nozzle temperature | 210 to 225 | °C | |
| Drying temperature | 100 to 110 | °C | |
| Drying time | 2.0 to 3.0 | hr | |
| Barrel 1 zone temperature | 160 to 200 | °C | |
| Barrel 3 zone temperature | 160 to 200 | °C | |
| Barrel 5 zone temperature | 160 to 200 | °C | |
| Connector temperature | 175 to 200 | °C | |
| Nozzle temperature | 175 to 205 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Die C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |