| About |
|---|
| XIRAN ® SG230 are styrene maleic anhydride (SMA) based injection molding compounds with: high thermal stability high dimensional stability excellent surface adhesion properties This product is available in standard black (XIRAN ® SG230) and in extra black version (XIRAN ® SG230EB-B). XIRAN ® SG230 (EB-B) XIRAN ® SG230 is a 15% glass filled injection molding compound designed for applications with high stiffness-strength. These products are very suitable for painted and foamed parts, high temperature resistance and precision parts with high shot to shot consistency.&& |
| Product Description | |
|---|---|
| Generic | Styrene-maleic anhydride copolymer |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Dimensional Stability,Foaming performance,Sprayable,High Heat Resistance,Good bond,Heat Stabilized |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.17 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 240℃，10.0kg | 10 | g/10min | ISO 1133 |
| Spiral flow length | 35.0 | cm | Internal Method |
| Shrinkage rate | |||
| TD | 0.63 | % | |
| MD | 0.33 | % | |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 0.20 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 5300 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 75.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 2.5 | % | ISO 527-2 |
| Bending modulus | 5400 | MPa | ISO 178 |
| bending strength | 120 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -40℃ | 8.0 | kJ/m² | |
| 23℃ | 9.0 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| -40℃ | 32 | kJ/m² | |
| 23℃ | 28 | kJ/m² | |
| Impact strength of cantilever beam notch | |||
| -40℃ | 8.0 | kJ/m² | |
| 23℃ | 9.0 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 120 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | 122 | ℃ | ISO 306/B |
| Linear coefficient of thermal expansion | |||
| MD：-30~80℃ | 4.2E-5 | 1/℃ | |
| TD：-30~80℃ | 5.5E-5 | 1/℃ |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 to 90 | °C | |
| Drying time | 2.0 to 3.0 | hr | |
| Barrel rear temperature | 240 to 295 | °C | |
| Barrel middle temperature | 240 to 295 | °C | |
| Barrel front temperature | 240 to 295 | °C | |
| Nozzle temperature | 240 to 295 | °C | |
| Processing (melt) temperature | < 295 | °C | |
| Back pressure | 0.500 to 1.50 | MPa | |
| Screw speed | 30 to 60 | rpm | |
| Mold Temperature | |||
| non visible parts | 40 to 80 | °C | |
| visible parts | 85 to 100 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Mold Temperature: 149°F, Melt Temperature: 482°F, Injection Pressure: 1.02E+3 psi |
| 3. Measured according to the Autodesk Mold flow Plastics Labs using a tag mold. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |