POCAN® AF4120 000000

soliao
2024年4月1日
PBT+ASA

About
POCAN® AF4120 000000 PBT+ASA, 20 % glass fibers, injection molding, flame retardant, low tendency to warp&&POCAN® AF4120 000000 PBT+ASA, 20 % glass fibers, injection molding, flame retardant, low tendency to warp&&POCAN® AF4120 000000 PBT+ASA, 20 % glass fibers, injection molding, flame retardant, low tendency to warp&&

Product Description
Supplier	LANXESS
Generic	PBT+ASA
Material Status	Commercial: Active
Features	Low warping,Flame Characteristics
Availabilitys	Africa & Middle East ,Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.54	g/cm³	ISO 1183
Melt Volume Rate
260℃，5 kg	40.0	cm³/10min	ISO 1133
Shrinkage rate
TD：120℃，2.0 mm	0.10	%
TD：250℃，2.0 mm	0.70	%
MD：120℃，2.0 mm	0.10	%
MD：250℃，2.0 mm	0.40	%

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength
Charpy Unnotch Impact strength
-30℃	35	kJ/m²
23℃	40	kJ/m²
Impact strength of cantilever beam notch
-30℃	< 10	kJ/m²
23℃	< 10	kJ/m²
Notched impact strength of cantilever beam
23℃	35	kJ/m²	ISO 180/1U

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	209	℃	ISO 75-2/B
1.8 MPa, unannealed	170	℃	ISO 75-2/A
Vicat Softening Temp
B50	155	℃	ISO 306
Ball pressure test
193℃	通过		IEC 60695-10-2
Melting temperature	225	℃	ISO 11357-3
Linear coefficient of thermal expansion
MD：23~55℃	3.0E-5	1/℃
TD：23~55℃	1.0E-4	1/℃

Electrical performance	Nominal value	Unit	Test method
Surface resistivity	2.0E+16	ohms	IEC 60093
Volume resistivity
23℃	8.0E+15	ohms·cm	IEC 60093
Dielectric strength
23 ℃，1 mm	35	kV/mm	IEC 60243-1
Compared to the leakage tracing index	PLC 2		UL 746
Compared to the leakage tracing index
Solution A	275	V	IEC 60112

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant level
0.40 mm	V-0
1.50 mm	V-0
Glowing wire flammability index
0.40 mm	960	℃
0.75 mm	960	℃
1.5 mm	960	℃
3.0 mm	960	℃
Igniting temperature of the hot wire
0.4 mm	900	℃
0.75 mm	825	℃
1.5 mm	725	℃
3 mm	750	℃
Extreme oxygen index	28	%	ISO 4589-2

Supplementary information	Nominal value	Unit	Test method
ISO Shortname	ISO 7792-1-PBT+ASA, GFMR, 07-070, GF20

MECHANICAL	Nominal value	Unit	Test method
Ball hardness	176	MPa	ISO 2039-1
Tensile modulus
23℃	7400	MPa	ISO 527-1-2
tensile strength
Fracture, 23 ℃	105	MPa	ISO 527-2/5
Tensile strain
Fracture, 23 ℃	2.4	%	ISO 527-2/5
Bending modulus
23℃	7400	MPa	ISO 178-A
bending strength
23℃	155	MPa	ISO 178-A
Bending strain	2.6	%	ISO 178/A

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature – Dehumidifying desiccant	120	°C
Drying time – Dehumidifying desiccant	4.0 to 8.0	hr
Processing (melt) temperature	240 to 260	°C
Mold temperature	80 to 100	°C
Residual Moisture Content	0.0 to 0.020	%	Karl Fisher

Notes
1. Typical properties: these are not to be construed as specifications.
2. 60x60x2mm, 4 hr
3. 60x60x2mm, 80°C MT, 600 bar
4. 0.079 in/min
5. 2 mm/min
6. 10°C/min
7. Solution A
8. Procedure A
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.