| Hifax CA 10 A is a reactor TPO (thermoplastic polyolefin) manufactured using the LyondellBasell proprietary Catalloy process technology. It is suitable for industrial applications where a combination of good processability and excellent softness is required. It is widely used as building block resin for flexible water-proofing membranes. Hifax CA 10 A exhibits low stiffness, low hardness and good impact resistance. The grade is available in natural pellet form.&& |
| Product Description | |
|---|---|
| Supplier | LyondellBasell |
| Generic | Polyolefin Elastomer |
| Material Status | Commercial: Active |
| Features | Excellent Processability,High impact resistance,Low Hardness,Heat Resistance, Good,Soft,High ESCR |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.880 | g/cm³ | ISO 1183/A |
| Melt Flow Rate | |||
| 230℃，2.16kg | 0.60 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 15 seconds | 30 | ISO 868 | |
| tensile strength | |||
| Yield, molding | 6.00 | MPa | ISO 527-2/500 |
| fracture | 11.0 | MPa | ISO 527-2 |
| Fracture, molded | 20.0 | MPa | ISO 527-2/500 |
| Tensile strain | |||
| fracture | > 500 | % | ISO 527-2 |
| Fracture, molded | 800 | % | ISO 527-2/500 |
| Bending modulus | 80.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -20℃ | No Break | ISO 180/1A | |
| 23℃ | No Break | ISO 180/1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 40.0 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| A50 | 60.0 | ℃ | ISO 306/A50 |
| Melting temperature | 142 | ℃ | ISO 11357-3 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |