| PC+ ABS Automotive applications&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.12 | g/cm³ | ASTM D792 , ISO 1183 |
| Shrinkage rate | Internal Method | ||
| MD：3.2 mm | 0.50 to 0.70 | % | Internal Method |
| TD：3.2 mm | 0.50 to 0.70 | % | Internal Method |
| Water absorption rate | ISO 62 | ||
| 23℃，24hr | 0.30 | % | ISO 62 |
| Saturation, 23 ℃ | 0.60 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.20 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 2250 | MPa | ASTM D638 |
| — | 2250 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 58.0 | MPa | ASTM D638 |
| yield | 58.0 | MPa | ISO 527-2/50 |
| fracture | 50.0 | MPa | ASTM D638 |
| fracture | 55.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 5.3 | % | ASTM D638 |
| yield | 5.2 | % | ISO 527-2/50 |
| fracture | 75 | % | ASTM D638 |
| fracture | 75 | % | ISO 527-2/50 |
| Bending modulus | |||
| 50 mm span | 2300 | MPa | ASTM D790 |
| — | 2300 | MPa | ISO 178 |
| bending strength | |||
| — | 85.0 | MPa | ISO 178 |
| Yield, 50 mm span | 87.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 25 | kJ/m² | ISO 179/1eA |
| 23℃ | 50 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 无断裂 | ISO 179/1eU | |
| 23℃ | 无断裂 | ISO 179/1eU | |
| Impact strength of cantilever beam notch | |||
| -30℃ | 300 | J/m | ASTM D256 |
| 23℃ | 600 | J/m | ASTM D256 |
| -30℃ | 25 | kJ/m² | ISO 180-1A |
| 23℃ | 50 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | ISO 180/1U | ||
| -30℃ | 无断裂 | ISO 180/1U | |
| 23℃ | 无断裂 | ISO 180/1U | |
| Dart impact equipped with measuring instruments | ASTM D3763 | ||
| -30℃，Total Energy | 90.0 | J | ASTM D3763 |
| 23℃，Total Energy | 90.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.2 mm | 128 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 3.2 mm | 110 | ℃ | ASTM D648 |
| Vicat Softening Temp | |||
| — | 131 | ℃ | ASTM D1525 9 |
| B120 | 133 | ℃ | ISO 306/B120 |
| Ball pressure test | IEC 60695-10-2 | ||
| 75℃ | 通过 | IEC 60695-10-2 | |
| 100℃ | 通过 | IEC 60695-10-2 | |
| Linear coefficient of thermal expansion | ASTM E831 | ||
| MD：-40~40℃ | 7.0E-5 | 1/℃ | ASTM E831 |
| TD：-40~40℃ | 8.0E-5 | 1/℃ | ASTM E831 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | > 1.0E+16 | ohms·cm | IEC 60093 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 95 to 105 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Hopper temperature | 60 to 80 | °C | |
| Barrel rear temperature | 230 to 260 | °C | |
| Barrel middle temperature | 250 to 290 | °C | |
| Barrel front temperature | 250 to 290 | °C | |
| Nozzle temperature | 240 to 280 | °C | |
| Processing (melt) temperature | 260 to 290 | °C | |
| Mold temperature | 60 to 90 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Type I, 2.0 in/min |
| 4. 0.051 in/min |
| 5. 0.079 in/min |
| 6. at Yield |
| 7. 80*10*4 sp=62mm |
| 8. 80*10*4 mm |
| 9. Rate A (50°C/h), Loading 2 (50 N) |
| 10. Approximate Maximum |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |