CYCOLAC™ S705 resin

About

Product Description
Supplier	SABIC
Generic	ABS
Material Status	Commercial: Active
Features	High impact resistance,Good liquidity,Electroplating
Availabilitys	North America,Latin America

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.05	g/cm³	ASTM D792
Shrinkage rate
MD
MD	0.5~0.7	%
Water absorption rate
Saturation, 23 ℃	1	%	ISO 62
23℃，50% RH	0.2	%	ISO 62
Melt Flow Rate
220℃，10.0kg	31	g/10min	ISO 1133
Melt Volume Rate
220℃，10 kg	33	cm³/10min	ISO 1133

MECHANICAL	Nominal value	Unit	Test method
Taber wear and tear	109	mg/1000cy
tensile strength
Yield, 5 mm/min	40	MPa	ISO 527
Fracture, 5 mm/min	35	MPa	ISO 527
Yield, 50 mm/min	45		ISO 527
Fracture, 50 mm/min	35		ISO 527
Tensile strain
Yield, 5 mm/min	2	%	ISO 527
Fracture, 5 mm/min	20	%	ISO 527
Yield, 50 mm/min	2	%	ISO 527
Fracture, 50 mm/min	30	%	ISO 527
Tensile modulus	2500	MPa	ISO 527
bending strength
yield	69	MPa	ISO 178
Bending modulus	2400	MPa	ISO 178
Rockwell hardness
R-level	112		ISO 2039-2

THERMAL	Nominal value	Unit	Test method
Thermal conductivity coefficient	0.2	W/m/℃	ISO 8302
Ball pressure test
75℃±2℃	PASSES		IEC 60695-10-2
Vicat Softening Temp
B50	97	℃	ISO 306
B120	100	℃	ISO 306
Hot deformation temperature
0.45 MPa, 100 mm span	90	℃	ISO 75/Be
1.8 MPa, 100 mm span	78	℃	ISO 75/Ae
Linear expansion coefficient (-40 ° C~40 ° C)
MD	8×10^-5	1/℃	ISO 11359-2
TD	8×10^-5	1/℃	ISO 11359-2
Relative temperature index
Electrical performance	60	℃	UL 746B
Impact mechanical performance	60	℃	UL 746B
Non mechanical impact performance	60	℃	UL 746B

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23℃	16	kJ/m²	ISO 180-1A
-30℃	6	kJ/m²	ISO 180-1A
Charpy impact strength
23℃	16	kJ/m²	ISO 180/1eA
-30℃	6	kJ/m²	ISO 180/1eA

Electrical performance	Nominal value	Unit	Test method
Volume resistivity	>1×10^15	ohms·cm	IEC 60093
Surface resistivity	1E+15	ohms	IEC 60093
Dielectric strength
0.8 mm in oil	35	kV/mm	IEC 60243-1
1.6 mm in oil	26	kV/mm	IEC 60243-1
3.2 mm in oil	18	kV/mm	IEC 60243-1
Relative permittivity
1 MHz	2.6		IEC 60250
50-60 Hz	2.7		IEC 60250
Dissipation factor
50-60 Hz	0.004		IEC 60250
1 MHz	0.008		IEC 60250
Compared to the leakage tracing index	600	V	IEC 60112

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant level
1.50 mm	HB		UL 94
2.50 mm	HB		UL 94
Burning wire flammability index 650 ° C passed	1	mm	IEC 60695-2-12

Process Conditions
injection molding	Nominal value	Unit	Test method
Dry conditions	Nominal value	Unit	Test method
Melt Temperature	250~270	℃
Nozzle temperature	240~260	℃
Front temperature	245~265	℃
Mid section temperature	240~260	℃
Post stage temperature	230~250	℃
Hopper temperature	60~80
Mold temperature	65~80	℃
drying temperature	85~95	℃
Drying time	2~4	hrs
Maximum moisture content	0.02	%

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.