| About |
|---|
| Thermoplastic Polyether-Polyurethane with outstanding hydrolysis resistance, low temperature flexibility and high resistance to micro-organisms, plasticized, phthalate-free.&& |
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | TPU-醚 |
| Material Status | Commercial: Active |
| Features | Hydrolysis stability,No DEHP plasticizer,Antimicrobial properties,Low temperature toughness |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.07 | g/cm³ | ISO 1183/A |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 20% strain | 1.00 | MPa | |
| 100% strain | 2.50 | MPa | |
| 300% strain | 4.50 | MPa | |
| tensile strength | 26.0 | MPa | DIN 53504-S2 |
| Tensile strain | |||
| fracture | 950 | % | DIN 53504-S2 |
| tear strength | 40 | kN/m | ISO 34-1 |
| Compression deformation | |||
| 23℃，72 hr | 40 | % | |
| 70℃，24 hr | 25 | % |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore A, 3 seconds | 63 | ISO 7619 | |
| Wear amount | 45.0 | mm³ | ISO 4649-A |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 to 90 | °C | |
| Drying time | 2.0 to 3.0 | hr | |
| Recommended maximum moisture content | 0.050 | % | |
| Barrel rear temperature | 180 to 200 | °C | |
| Barrel middle temperature | 185 to 205 | °C | |
| Barrel front temperature | 190 to 210 | °C | |
| Nozzle temperature | 190 to 210 | °C | |
| Processing (melt) temperature | 190 to 210 | °C | |
| Mold temperature | 15 to 70 | °C | |
| Injection speed | 慢 | ||
| Back pressure | 5.00 to 15.0 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Method Bb, Angle (Nicked) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |