| PEEK-OPTIMA® polymer from Invibio® is a high performance biomaterial providing advanced solutions for implant manufacturers. Formulated to meet the most exacting in-vivo criteria, PEEK-OPTIMA is biocompatible, safe and stable. Manufacturers of cardiovascular, dental, neurological and orthopaedic implants choose PEEK-OPTIMA for its: Excellent mechanical performance High wear resistance Ability to be repeatedly sterilized without impairing performance Biocompatibility Drug and Device Master Files lodged with the FDA Invibio offers a ‘no-change’ agreement for the assured long-term supply of PEEK-OPTIMA. This guarantees its specification and production methods over an agreed period of time.&& |
| Product Description | |
|---|---|
| Generic | PEEK |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Low extract,High purity,Good disinfection,Steam sterilized,Low Residuals,Hydrolysis stability,Biocompatible,Radiation disinfection,Good stability,Good wear resistance,Ethylene oxide disinfection |
| Availabilitys | North America,Europe |
| Technical Data | |||
|---|---|---|---|
| IMPACT | Nominal value | Unit | Test method |
| Impact strength of cantilever beam notch | ISO 180 | ||
| — | 7.5 | kJ/m² | ISO 180 |
| — | 4.7 | kJ/m² | ISO 180 |
| Notched impact strength of cantilever beam | 无断裂 | ISO 180 | |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 340 | ℃ | |
| Linear coefficient of thermal expansion | |||
| MD | ASTM D696 | ||
| — | 4.7E-5 | cm/cm/℃ | ASTM D696 |
| — | 1.1E-4 | cm/cm/℃ | ASTM D696 |
| Relative temperature index | 260 | ℃ | UL 746 |
| Electrical performance | 260 | ℃ | UL 746 |
| Impact mechanical performance | 260 | ℃ | UL 746 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| M-level | 99 | ASTM D785 | |
| tensile strength | ISO 527-2 | ||
| yield | 100 | MPa | ISO 527-2 |
| yield | 115 | MPa | ISO 527-2 |
| Tensile strain | ISO 527-2 | ||
| fracture | 40 | % | ISO 527-2 |
| fracture | 20 | % | ISO 527-2 |
| Bending modulus | ISO 178 | ||
| — | 4100 | MPa | ISO 178 |
| — | 4000 | MPa | ISO 178 |
| bending strength | ISO 178 | ||
| — | 165 | MPa | ISO 178 |
| — | 170 | MPa | ISO 178 |
| compressive strength | 135 | MPa | ISO 604 |
| shear modulus | 1150 | MPa | ISO 15310 |
| shear strength | 90.0 | MPa | ASTM D732 |
| Poisson’s ratio | 0.36 | ASTM D638 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.30 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD：210℃ | 1.2 | % | |
| Water absorption rate | |||
| 23℃，24hr | 0.50 | % | ISO 62 |
| Apparent viscosity of melt | 0.440 | kPa | Internal Method |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Rod |
| 3. Below Tg |
| 4. Above Tg |
| 5. Capillary Rheometer |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |