| About |
|---|
| CALIBRE™ 200-3 polycarbonate resin is produced in compliance with the US Food and Drug Administration (FDA) and EU food contact regulations. This resin provides excellent impact resistance, heat distortion resistance and optical clarity as well as high melt strength for sheet extrusion applications. Available in natural color only. Main Characteristics: U.S. FDA 21 CFR 177.1580 CSA NSF Underwriters Laboratory (UL) EU food contact 2011/10/EC Applications: Small appliances Sheet and profile extrusion Housewares&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Good Clarity,High impact resistance,Food contact compliance,Good melt strength,HB |
| Availabilitys | North America,Latin America,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ASTM D792 |
| Density | 1.20 | g/cm³ | ISO 1183/B |
| Melt Flow Rate | |||
| 300℃，1.20kg | 3.0 | g/10min | ASTM D1238 |
| 300℃，1.20kg | 3.0 | g/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 0.50 to 0.70 | % | ISO 294-4 |
| MD | 0.50 to 0.70 | % | ASTM D955 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 0.32 | % | ASTM D570 |
| Equilibrium, 23 ℃, 50% RH | 0.32 | % | ISO 62 |
| 23℃，24hr | 0.15 | % | ISO 62 |
| 23℃，24hr | 0.15 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 93 | kJ/m² | ISO 180-A |
| 23℃ | 960 | J/m | ASTM D256 |
| 23℃ | No Break | ASTM D256 | |
| Notched impact strength of cantilever beam | |||
| 23℃ | No Break | ISO 180 | |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 93.8 | J | ASTM D3763 |
| Tensile impact strength | 630 | kJ/m² | ASTM D1822 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed | 143 | ℃ | ISO 75-2/A |
| 1.8 MPa, annealed | 143 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 132 | ℃ | ISO 75-2/A |
| 1.8 MPa, unannealed | 132 | ℃ | ASTM D648 |
| 0.45 MPa, annealed | 146 | ℃ | ASTM D648 |
| 0.45 MPa, annealed | 146 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | 151 | ℃ | ASTM D1525 6 |
| B50 | 151 | ℃ | ISO 306 |
| Linear coefficient of thermal expansion | |||
| MD：-40~82℃ | 6.8E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 2.0E+17 | ohms·cm | ASTM D257 |
| Dielectric strength | 17 | kV/mm | ASTM D149 |
| Dielectric strength | 17 | kV/mm | IEC 60243-1 |
| Dielectric constant | ASTM D150 | ||
| 60 Hz | 3.00 | ASTM D150 | |
| 1 MHz | 3.00 | ASTM D150 | |
| Dissipation factor | ASTM D150 | ||
| 60 Hz | 1.0E-3 | ASTM D150 | |
| 1 MHz | 2.0E-3 | ASTM D150 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.60 mm | HB | UL 94 | |
| 3.20 mm | HB | UL 94 | |
| Extreme oxygen index | 26 | % | ISO 4589-2 |
| Average combustion degree | 3 | cm | ASTM D635 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Refractive index | 1.586 | ASTM D542 | |
| Refractive index | 1.586 | ISO 489 | |
| Transmittance | 89.0 | % | ASTM D1003 |
| Haze | 1.0 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2480 | MPa | ASTM D638 |
| Tensile modulus | 2480 | MPa | ISO 527-2/50 |
| tensile strength | |||
| fracture | 72.4 | MPa | ASTM D638 |
| fracture | 72.0 | MPa | ISO 527-2/50 |
| yield | 60.0 | MPa | ASTM D638 |
| yield | 60.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | 150 | % | ASTM D638 |
| fracture | 150 | % | ISO 527-2/50 |
| Bending modulus | 2410 | MPa | ASTM D790 |
| Bending modulus | 2410 | MPa | ISO 178 |
| bending strength | 96.5 | MPa | ASTM D790 |
| bending strength | 96.0 | MPa | ISO 178 |
| Taber abraser | 45 | % | ASTM D1044 |
| Rockwell hardness | ASTM D785 | ||
| M-level | 74 | ASTM D785 | |
| R-level | 118 | ASTM D785 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. Method I (3 point load), 0.079 in/min |
| 4. 0.079 in/min |
| 5. 11.1 ft/sec |
| 6. Rate A (50°C/h), Loading 2 (50 N) |
| 7. This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |