| Mineral filled PC/PET blend with high flow, high heat, dimensional stability, low shrinkage and low CTE, especially for painted applications&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PC+PET |
| Material Status | Commercial: Active |
| Features | Low CLTE,Good Dimensional Stability,High liquidity,Sprayable,Low contractility,High Heat Resistance |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.33 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 265℃，5.0kg | 28 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 265℃，5 kg | 24.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 0.50 to 0.60 | % | Internal Method |
| Water absorption rate | ISO 62 | ||
| Saturation, 23 ℃ | 0.42 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.14 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 3990 | MPa | ISO 527-1-2 |
| tensile strength | ISO 527-2/5 | ||
| yield | 53.0 | MPa | ISO 527-2/5 |
| fracture | 34.0 | MPa | ISO 527-2/5 |
| Tensile strain | ISO 527-2/5 | ||
| yield | 3.4 | % | ISO 527-2/5 |
| fracture | 21 | % | ISO 527-2/5 |
| Bending modulus | 3820 | MPa | ISO 178 |
| bending strength | 90.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 14 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -30℃ | 6.0 | kJ/m² | ISO 180-1A |
| 23℃ | 8.0 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | ISO 180/1U | ||
| -30℃ | 120 | kJ/m² | ISO 180/1U |
| 23℃ | 140 | kJ/m² | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 64 mm span | 100 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | |||
| B50 | 137 | ℃ | ISO 306 |
| B120 | 140 | ℃ | ISO 306/B120 |
| Linear coefficient of thermal expansion | ISO 11359-2 | ||
| MD：-30~80℃ | 4.5E-5 | 1/℃ | ISO 11359-2 |
| TD：-30~80℃ | 9.7E-5 | 1/℃ | ISO 11359-2 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 110 to 120 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Hopper temperature | 60 to 80 | °C | |
| Barrel rear temperature | 240 to 270 | °C | |
| Barrel middle temperature | 250 to 275 | °C | |
| Barrel front temperature | 260 to 280 | °C | |
| Nozzle temperature | 260 to 275 | °C | |
| Processing (melt) temperature | 265 to 275 | °C | |
| Mold temperature | 60 to 100 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Tensile Bar |
| 3. 0.079 in/min |
| 4. Yield |
| 5. 80*10*4 sp=62mm |
| 6. 80*10*4 |
| 7. 80*10*4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |