| About |
|---|
| 改性聚丙烯,良好的加工性能，高韧性，低翘曲 |
| Product Description | |
|---|---|
| Supplier | Kingfa |
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Low warping,Excellent Processability,Good flexibility |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| tensile strength | |||
| 50 mm/min | 18 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 50 mm/min | 100 | % | ASTM D638 |
| bending strength | |||
| 2 mm/min | 25 | MPa | ASTM D790 |
| Bending modulus | |||
| 2 mm/min | 1400 | MPa | ASTM D790 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa | 90 | ℃ | ASTM D648 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 10^16 | ohms·cm | ASTM D257 |
| other | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 350 | J/m | ASTM D256 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melt Flow Rate | |||
| 230℃，2.16Kg | 18 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| 23℃ | 1.1-1.5 | % | ASTM D955 |
| Density | 1.08 | g/cm³ | ASTM D792 |
| Process Conditions | |||
|---|---|---|---|
| injection molding | Nominal value | Unit | Test method |
| Melt temperature | 190-245 | °C | |
| Temperature of the rear section of the barrel | 180-210 | °C | |
| Temperature in the middle section of the barrel | 190-230 | °C | |
| Temperature of the front section of the material barrel | 200-240 | °C | |
| Mold temperature | 30-60 | °C | |
| Processing upper limit temperature | 260 | °C | |
| Injection molding speed | 低速to中速 | ||
| Back pressure | 10 | KPa | |
| Pre-drying | 90°C, 2hr | ||
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |