Low-flexural-strength nylon 6/polyethylene alloy Pamphlet: Low-flexural-strength nylon 6/polyethylene alloy is authorized as patent product of our company. This material has low flexural strength, good flexibility, still maintain basically mechanical properties after six times repeated extrusion process, good processing performance, extrusion process stability, uniform diameter of extruded nylon rod, smooth surface. The material can be used to extruded nylon rod and tube, double-wall corrugated pipe, extruded nylon core material and other extrusion products.&&

About

Low-flexural-strength nylon 6/polyethylene alloy Pamphlet: Low-flexural-strength nylon 6/polyethylene alloy is authorized as patent product of our company. This material has low flexural strength, good flexibility, still maintain basically mechanical properties after six times repeated extrusion process, good processing performance, extrusion process stability, uniform diameter of extruded nylon rod, smooth surface. The material can be used to extruded nylon rod and tube, double-wall corrugated pipe, extruded nylon core material and other extrusion products.&&

Product Description
Supplier	Lihan
Generic	PA6
Material Status	Commercial: Active
Features	Excellent Processability,Good flexibility,HB
Availabilitys	Asia Pacific
Process Methods	Extrusion

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.10	g/cm³	ISO 1183
Shrinkage rate	0.90 to 1.3	%

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch	60	kJ/m²	ISO 180

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	60.0	℃	ISO 75-2/A
Melting temperature	220	℃	DSC

Electrical performance	Nominal value	Unit	Test method
Surface resistivity	1.0E+14	ohms	ASTM D257
Compared to the leakage tracing index	600	V	IEC 60112

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant level	HB		UL 94

MECHANICAL	Nominal value	Unit	Test method
Rockwell hardness
R-level	100		ISO 2039-2
tensile strength
fracture	48.0	MPa	ISO 527-2
Tensile strain
fracture	100	%	ISO 527-2
Bending modulus	750	MPa	ISO 178
bending strength	30.0	MPa	ISO 178

Process Conditions
Extrusion	Nominal value	Unit	Test method
Melt temperature	230 to 250	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.