| A continuous unidirectional “E” fiberglass combined with a 50/50 woven fiberglass inlay that has high strength and stiffness along the longitudinal (0) axis and provides cross strength (90 degrees to the longitudinal axis). GC-70-ULS is manufactured with a proprietary pulforming process in which all glass fibers are pretensioned and aligned during the impregnation and curing process.&& |
| Product Description | |
|---|---|
| Supplier | Polyone |
| Generic | 热固性复合材料 |
| Material Status | Commercial: Active |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.88 | g/cm³ | ASTM D1505 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 41400 | MPa | ASTM D3039 |
| tensile strength | 1050 | MPa | ASTM D3039 |
| Tensile strain | |||
| fracture | 2.5 | % | ASTM D3039 |
| Bending modulus | 41400 | MPa | ASTM D790 |
| bending strength | 1450 | MPa | ASTM D790 |
| Compression modulus | 41400 | MPa | ASTM D3410 |
| compressive strength | 820 | MPa | ASTM D3410 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass transition temperature | 121 | ℃ | ASTM D3418 |
| Notes |
|---|
| 1. Width: .1.50″ to 18.00″ Thickness: .040″ to .080″ Length: 6″ to 120″ |
| 2. Typical properties: these are not to be construed as specifications. |
| 3. 0 degree orientation |
| 4. Strength Values developed from ASTM D790 are dependent on thickness. As thickness increased flex strength decreased. The test data above is based on a test thickness of .060″ |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |