| About |
|---|
| Durethan® DP2802/30 000000 (Dry) PA 66, 30 % glass fibers, injection molding, halogen free flame retardant&&Durethan® DP2802/30 000000 PA 66, 30 % glass fibers, injection molding, halogen free flame retardant&&Durethan® DP2802/30 000000 PA 66, 30 % glass fibers, injection molding, halogen free flame retardant&& |
| Product Description | |
|---|---|
| Supplier | LANXESS |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Halogen free,Flame Characteristics |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.40 | g/cm³ | ISO 1183 |
| viscosity | 127 | g/cm³ | ISO 1628 |
| Shrinkage rate | |||
| MD | 0.64 | % | ISO 294-4 |
| TD | 0.77 | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 23℃ | 85.0 | MPa | ISO 527-2 |
| Yield, 23 ℃ | – | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 3.5 | % | ISO 527-2 |
| Yield, 23 ℃ | – | % | ISO 527-2 |
| Tensile modulus | |||
| 23℃ | 6000 | MPa | ISO 527-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 250 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, annealed | 155 | ℃ | ISO 75-2/Af |
| Melting temperature | 263 | ℃ | ISO 11357-3 |
| Vicat Softening Temp | |||
| Linear coefficient of thermal expansion | |||
| MD | 7.1E-5 | 1/℃ | ISO 11359-2 |
| TD | 3.9E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Insulation strength | |||
| 33.0 | KV/mm | IEC 60243-1 | |
| Dissipation factor | |||
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.75mm | V-2 | UL 94 | |
| 1.00mm | V-2 | UL 94 | |
| 1.50mm | V-2 | UL 94 | |
| 3.00mm | V-2 | UL 94 | |
| Igniting temperature of the hot wire | |||
| 0.75 mm | 850 | ℃ | IEC 60695-2-12 |
| 0.75 mm | 775 | ℃ | IEC 60695-2-12 |
| Relative temperature of heating wire | |||
| 0.75mm | 960 | ℃ | IEC 60695-2-13 |
| 1.00mm | 960 | ℃ | IEC 60695-2-13 |
| 1.50mm | 960 | ℃ | IEC 60695-2-13 |
| 3.00mm | 960 | ℃ | IEC 60695-2-13 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 35.0 | kJ/m² | ISO 179/1eU |
| Charpy Notched Impact Strength | |||
| 23℃ | <=10.0 | kJ/m² | ISO 179/1eA |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 60x60x2mm, 4 hr |
| 3. 60x60x2mm, 80°C MT, 600 bar |
| 4. 0.079 in/min |
| 5. 2 mm/min |
| 6. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |