| About |
|---|
| Ixef® 1622 is an impact modified, 50% glass-fiber reinforced polyarylamide. which exhibits very high strength and rigidity, outstanding surface gloss, and excellent impact resistance. Natural: Ixef® 1622/0003 Black: Ixef® 1622/9003 Custom Colorable&& |
| Product Description | |
|---|---|
| Supplier | Solvay |
| Generic | Paraformaldehyde |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good flexibility,Good surface appearance,High impact resistance,Good Dimensional Stability,High liquidity,Solvent resistance,Low moisture absorption |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.60 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD | 0.10 to 0.30 | % | Internal Method |
| Water absorption rate | Internal Method | ||
| 23℃，24hr | 0.19 | % | ISO 62 |
| Balance, 65% RH | 1.5 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 17000 | MPa | ISO 527-2 |
| tensile strength | |||
| yield | 235 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 2.6 | % | ISO 527-2 |
| Bending modulus | 17000 | MPa | ISO 178 |
| bending strength | 360 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Notched impact strength of cantilever beam | 120 | J/m | ASTM D256 |
| Impact strength of cantilever beam notch | 1100 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 220 | ℃ | ISO 75-2/A |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric constant | |||
| 2.40 GHz | 4.27 | ASTM D2520 | |
| Dissipation factor | |||
| 2.40 GHz | 0.0095 | ASTM D2520 | |
| Dielectric strength | 25 | kV/mm | IEC 60243-1 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.6 mm | HB | UL 94 | |
| Extreme oxygen index | 25 | % | ISO 4589-2 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 120 | °C | |
| Drying time | 0.50 to 1.5 | hr | |
| Temperature at the rear of the barrel | 250 to 260 | °C | |
| Front temperature of material barrel | 260 to 280 | °C | |
| Processing (melt) temperature | 270 | °C | |
| Mold temperature | 120 to 140 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Solvay Internal procedure, Pressure 750 bars (10.9 kpsi); specimen 40 mm x 20 mm x 2-4 mm. (1.6 in. x 0.8 in. x 0.08-0.16 in.) |
| 3. Method B |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |