| 30% Mineral/Glass-Reinforced Nylon Resin (PA6), Ford Color Match&& |
| Product Description | |
|---|---|
| Supplier | Wellman |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.38 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| TD：23℃ | 0.60 to 1.0 | % | |
| MD：23℃ | 0.30 to 0.70 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 23 ℃, injection molding | 105 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃, injection molding | 2.0 | % | ISO 527-2 |
| Bending modulus | |||
| 23 ℃, injection molding | 7800 | MPa | ISO 178 |
| bending strength | |||
| 23 ℃, injection molding | 160 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23 ℃, injection molding | 4.3 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 200 | ℃ | ISO 75-2/A |
| Melting temperature | |||
| DSC | 220 | ℃ | ISO 3146 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 175 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.15 | % | |
| Barrel rear temperature | 260 to 288 | °C | |
| Barrel middle temperature | 254 to 288 | °C | |
| Barrel front temperature | 249 to 288 | °C | |
| Nozzle temperature | 243 to 288 | °C | |
| Processing (melt) temperature | 260 to 288 | °C | |
| Mold temperature | 71 to 93 | °C | |
| Injection pressure | 34.0 to 138 | MPa | |
| Back pressure | 0.340 to 1.03 | MPa | |
| Screw speed | 30 to 120 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |