CYCOLOY™ RCX7233 Resin

About
CYCOLOY™ RCX7233 是PC与非溴化和非氯化阻燃剂的混合的冲击改性的树脂。通过注塑成型，符合UL-94 V0 防火等级，具有优良的流动性和冲击平衡，薄壁阻燃性。仅适用于有限的颜色。

Product Description
Supplier	SABIC
Generic	PC+ABS
Material Status	Commercial: Active
Features	Good liquidity,Rigid-tough balance
Availabilitys	Asia Pacific

Technical Data
MECHANICAL	Nominal value	Unit	Test method
tensile strength
Fracture, Type I, 50 mm/min	55	MPa	ASTM D638
Yield, Type I, 50 mm/min	60	MPa	ASTM D638
Tensile strain
Fracture, Type I, 50 mm/min	60	%	ASTM D638
Yield, Type I, 50 mm/min	4	%	ASTM D638
Tensile modulus
5 mm/min	2500	MPa	ASTM D638
bending strength
Yield, 1.30 mm/min, n, 50 mm span	100	MPa	ASTM D790
Bending modulus
1.30 mm/min, n, 50 mm span	2400	MPa	ASTM D790

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23℃	690	J/m	ASTM D256
Impact strength of cantilever beam notch
-30℃	130	J/m	ASTM D256
Total energy of instrument impact
23℃	57	J	ASTM D 3763
Impact strength of cantilever beam notch
23℃，80103	50	kJ/m²	ISO 180-1A

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp	107	℃	ASTM D1525
Hot deformation temperature
1.8 MPa, unannealed, 6.4 mm span	93	℃	ASTM D648
1.8 MPa, unannealed, 3.2 mm span	87	℃	ASTM D648
Hot deformation temperature
0.45 MPa, unannealed, 6.4 mm	103	℃	ASTM D648
Linear coefficient of thermal expansion
TD：-40~40℃	7.5E-05	1/℃	ASTM E831
MD：-40~40℃	7.5E-05	1/℃	ASTM E831

PHYSICAL	Nominal value	Unit	Test method
Density	1.19		ASTM D792
Shrinkage rate
MD：3.2 mm	0.4 – 0.6	%	Internal Method
Melt Flow Rate
260℃，2.16kg	19	g/10min	ASTM D1238
Water absorption rate
Saturation, 23 ℃	0.15	%	ISO 62

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
94V-1 flame level	0.4	mm	UL 94 by SABIC-IP
94V-0 flame level	0.75	mm	UL 94 by SABIC-IP

Process Conditions
injection molding	Nominal value	Unit	Test method
Drying temperature	80 – 90	°C
Drying time	2 – 4	hrs
Maximum water content	0.02	%
Melt temperature	250 – 300	°C
Nozzle temperature	250 – 300	°C
Front Section Zone 3 Temperature	250 – 300	°C
Temperature in Zone 2 of the middle section	240 – 300	°C
Temperature in Zone 1 of the rear section	230 – 300	°C
Hopper temperature	60 – 80	°C
Mold temperature	60 – 85	°C
Depth of exhaust groove	0.03 – 0.075	mm

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.