Ultramid® 8232G HS FR BK-102

About
Ultramid 8232G HS FR BK102 is a 25% glass fiber reinforced, heat stabilized, flame retardant pigmented black PA6 injection molding compound exhibiting excellent melt stability characteristics. It combines flame retardant ability with an excellent balance of high strength, stiffness and heat distortion temperature. Applications Ultramid 8232G HS FR BK102 is generally recommended for applications such as connectors, terminal blocks, switches and receptacles, coil bobbins, and appliance housings.&&

About

Ultramid 8232G HS FR BK102 is a 25% glass fiber reinforced, heat stabilized, flame retardant pigmented black PA6 injection molding compound exhibiting excellent melt stability characteristics. It combines flame retardant ability with an excellent balance of high strength, stiffness and heat distortion temperature. Applications Ultramid 8232G HS FR BK102 is generally recommended for applications such as connectors, terminal blocks, switches and receptacles, coil bobbins, and appliance housings.&&

Product Description
Supplier	BASF
Generic	PA6
Material Status	Commercial: Active
Features	Good Rigidity,Flame Characteristics,Heat Stabilized,Higher melt stability,V-0
Availabilitys	North America
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.62	g/cm³	ASTM D792
Shrinkage rate
MD：3.2 mm	0.30	%
Water absorption rate
saturated	4.0	%	ASTM D570
Balance, 50% RH	1.1	%	ASTM D570

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23℃	80	J/m	ASTM D256

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	205	℃	ASTM D648
Melting peak temperature	220	℃	ASTM D3418
0.8 mm	130	℃	UL 746
1.5 mm	130	℃	UL 746
2.5 mm	130	℃	UL 746
3.0 mm	130	℃	UL 746
Relative temperature index
Electrical performance			UL 746
Strength mechanical performance			UL 746
Impact mechanical performance			UL 746
0.8 mm	115	℃	UL 746
2.5 mm	115	℃	UL 746
3.0 mm	115	℃	UL 746
0.8 mm	105	℃	UL 746
1.5 mm	115	℃	UL 746
3.0 mm	120	℃	UL 746

FLAME CHARACTERISTICS	Nominal value	Test method
Flame retardant level		UL 94
0.80 mm	V-0	UL 94
1.50 mm	V-0	UL 94
2.50 mm	V-0 5VA	UL 94
3.00 mm	V-0 5VA	UL 94

MECHANICAL	Nominal value	Unit	Test method
tensile strength
Fracture, 23 ℃	145	MPa	ASTM D638
Tensile strain
Fracture, 23 ℃	2.5	%	ASTM D638
Bending modulus
23℃	9170	MPa	ASTM D790
bending strength
23℃	210	MPa	ASTM D790
Rockwell hardness
R-level	121		ASTM D785

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	80	°C
Drying time	2.0 to 4.0	hr
Recommended maximum moisture content	0.15	%
Processing (melt) temperature	250 to 290	°C
Mold temperature	80 to 95	°C
Injection pressure	3.50 to 12.5	MPa
Injection speed	Fast

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.