| About |
|---|
| PTFE filled, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL 94 V0 and 5VA listing in recognized colors.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polyetherimide |
| Material Status | Commercial: Active |
| Features | ECO,V-0 |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.33 | g/cm³ | ASTM D792 |
| Density | 1.33 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 337℃，6.60kg | 9.5 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 360℃，5 kg | 13.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | Internal Method | ||
| MD | 0.60 to 0.80 | % | Internal Method |
| MD：3.2 mm | 0.50 to 0.70 | % | Internal Method |
| Shrinkage rate | |||
| TD：3.2 mm | 0.50 to 0.70 | % | Internal Method |
| Water absorption rate | |||
| Saturation, 23 ℃ | 1.1 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.60 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 3460 | MPa | ASTM D638 |
| Tensile modulus | 3300 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 85.0 | MPa | ASTM D638 |
| fracture | 80.0 | MPa | ISO 527-2/50 |
| yield | 100 | MPa | ISO 527-2/50 |
| yield | 105 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 40 | % | ASTM D638 |
| fracture | 25 | % | ISO 527-2/50 |
| yield | 6.0 | % | ISO 527-2/50 |
| yield | 5.0 | % | ASTM D638 |
| Bending modulus | 3100 | MPa | ISO 178 |
| 50 mm span | 3550 | MPa | ASTM D790 |
| bending strength | 130 | MPa | ISO 178 |
| bending strength | |||
| Yield, 50 mm span | 155 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 11 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃ | 120 | J/m | ASTM D256 |
| 23℃ | 120 | J/m | ASTM D256 |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -30℃ | 8.0 | kJ/m² | ISO 180-1A |
| 23℃ | 10 | kJ/m² | ISO 180-1A |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 380 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 1.8 MPa, unannealed, 100 mm span | 190 | ℃ | ISO 75-2/Ae |
| 1.8 MPa, unannealed, 3.2 mm | 197 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.4 mm | 200 | ℃ | ASTM D648 |
| Vicat Softening Temp | 219 | ℃ | ASTM D1525 11 |
| Vicat Softening Temp | |||
| B50 | 215 | ℃ | ISO 306 |
| B120 | 210 | ℃ | ISO 306/B120 |
| Ball pressure test | |||
| 125℃ | Pass | IEC 60695-10-2 | |
| Linear coefficient of thermal expansion | |||
| TD：23~150℃ | 4.0E-5 | 1/℃ | ISO 11359-2 |
| TD：-40~150℃ | 4.0E-5 | 1/℃ | ASTM E831 |
| MD：23~150℃ | 3.9E-5 | 1/℃ | ISO 11359-2 |
| MD：-40~150℃ | 3.9E-5 | 1/℃ | ASTM E831 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.40 mm | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 135 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Drying time, maximum | 10 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Recommended injection volume | 40 to 60 | % | |
| Barrel rear temperature | 338 to 360 | °C | |
| Barrel middle temperature | 343 to 366 | °C | |
| Barrel front temperature | 349 to 371 | °C | |
| Nozzle temperature | 349 to 371 | °C | |
| Processing (melt) temperature | 349 to 371 | °C | |
| Mold temperature | 135 to 163 | °C | |
| Back pressure | 0.345 to 0.689 | MPa | |
| Screw speed | 40 to 70 | rpm | |
| Vent depth | 0.025 to 0.076 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Tensile Bar |
| 3. 0.20 in/min |
| 4. Type I, 0.20 in/min |
| 5. 0.051 in/min |
| 6. 0.079 in/min |
| 7. at Yield |
| 8. 80*10*4 sp=62mm |
| 9. 80*10*4 mm |
| 10. 120*10*4 mm |
| 11. Rate A (50°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |