| About |
|---|
| Features: Excellent mechanical properties. Excellent processability. Applications: Film for automatic packaging. General purpose bags.&& |
| Product Description | |
|---|---|
| Generic | LDPE+LLDPE |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Smoothness,High anti-blocking,Inoxidizability,Low density |
| Availabilitys | Latin America |
| Process Methods | Film extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.922 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 2.5 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 50 | µm | |
| Membrane puncture force | |||
| 50 µm | 8.83 | N | ASTM D3420 |
| tensile strength | ASTM D882 | ||
| MD, fracture, 50 µ m | 22.0 | MPa | ASTM D882 |
| TD, fracture, 50 µ m | 19.0 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD, fracture, 50 µ m | 250 | % | ASTM D882 |
| TD, fracture, 50 µ m | 650 | % | ASTM D882 |
| Elmandorf tear strength | ASTM D1922 | ||
| MD：50 µm | 230 | g | ASTM D1922 |
| TD：50 µm | 300 | g | ASTM D1922 |
| Impact Resistance（Film） | 270 | J/cm | ASTM D1709 |
| Toughness，Film | ASTM D882 | ||
| MD | 45.0 | MPa | ASTM D882 |
| TD | 80.0 | MPa | ASTM D882 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Transmittance | |||
| 50.0 µm | 83.0 | % | ASTM D1003 |
| Haze | |||
| 50 µm | 11 | % | ASTM D1003 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 130 to 180 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |