| About |
|---|
| LNP LUBRILOY LEXAN_WR6300 compound is a wear resistant PC+SAN, with proprietary lubricant, for business equipment applications.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | AES+PC+AS(SAN) |
| Material Status | Commercial: Active |
| Features | Lubricating,HB |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.17 | g/cm³ | ASTM D792 |
| Melt Volume Rate | |||
| 300℃，2.16 kg | 38.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.50 to 0.70 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 61.4 | MPa | ASTM D638 |
| yield | 60.7 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 160 | % | ASTM D638 |
| Bending modulus | |||
| 50 mm span | 2490 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 50 mm span | 96.5 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| 23℃ | 2500 | J/m | ASTM D4812 |
| -30℃ | 170 | J/m | ASTM D256 |
| 23℃ | 680 | J/m | ASTM D256 |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 60.2 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.4 mm | 134 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 3.2 mm | 117 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.4 mm | 121 | ℃ | ASTM D648 |
| Vicat Softening Temp | 137 | ℃ | ASTM D1525 4 |
| Linear coefficient of thermal expansion | |||
| TD：-40~40℃ | 1.2E-4 | 1/℃ | ASTM E831 |
| MD：-40~40℃ | 1.1E-4 | 1/℃ | ASTM E831 |
| Relative temperature index | |||
| Electrical performance | 80.0 | ℃ | UL 746 |
| Strength mechanical performance | 80.0 | ℃ | UL 746 |
| Impact mechanical performance | 80.0 | ℃ | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 107 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Drying time, maximum | 24 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Recommended injection volume | 40 to 60 | % | |
| Barrel rear temperature | 227 to 249 | °C | |
| Barrel middle temperature | 238 to 260 | °C | |
| Barrel front temperature | 249 to 271 | °C | |
| Nozzle temperature | 243 to 266 | °C | |
| Processing (melt) temperature | 249 to 271 | °C | |
| Mold temperature | 49 to 82 | °C | |
| Back pressure | 0.345 to 0.689 | MPa | |
| Screw speed | 40 to 70 | rpm | |
| Vent depth | 0.025 to 0.076 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type I, 2.0 in/min |
| 3. 0.051 in/min |
| 4. Rate A (50°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |