| About |
|---|
| This is a PC/ABS compound with colorable, good plating, surface and mechanical performance, a good candidate for Laser Direct Structuring applications&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | Good surface appearance,Electroplating,Good coloring |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.22 | g/cm³ | ASTM D792 |
| Melt Volume Rate | |||
| 260℃，5 kg | 14.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | ASTM D955 | ||
| MD：24 hrs | 0.60 | % | |
| TD：24 hrs | 0.60 | % | |
| Water absorption rate | ASTM D570 | ||
| 24hr | 0.010 | % | |
| 24hr，50% RH | 0.010 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2350 | MPa | ASTM D638 |
| tensile strength | ASTM D638 | ||
| yield | 47.0 | MPa | |
| fracture | 46.0 | MPa | |
| Tensile strain | ASTM D638 | ||
| yield | 4.6 | % | |
| fracture | 75 | % | |
| Bending modulus | |||
| 50 mm span | 2230 | MPa | ASTM D790 |
| bending strength | ASTM D790 | ||
| Yield, 50 mm span | 79.0 | MPa | |
| Fracture, 50 mm span | 78.0 | MPa |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 550 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 106 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | ASTM E831 | ||
| MD：-40~40℃ | 7.1E-5 | 1/℃ | |
| TD：-40~40℃ | 7.6E-5 | 1/℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Relative permittivity | |||
| 1.00 GHz | 2.94 | IEC 60250 | |
| Dissipation factor | |||
| 1 GHz | 5.7E-3 | IEC 60250 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 85.0 to 96.1 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Drying time, maximum | 8.0 | hr | |
| Recommended maximum moisture content | 0.010 | % | |
| Recommended injection volume | 50 to 70 | % | |
| Barrel rear temperature | 199 to 249 | °C | |
| Barrel middle temperature | 216 to 254 | °C | |
| Barrel front temperature | 216 to 254 | °C | |
| Nozzle temperature | 218 to 260 | °C | |
| Processing (melt) temperature | 218 to 260 | °C | |
| Mold temperature | 37.8 to 76.7 | °C | |
| Back pressure | 0.517 to 0.862 | MPa | |
| Screw speed | 50 to 100 | rpm | |
| Vent depth | 0.038 to 0.051 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. Type I, 2.0 in/min |
| 4. 0.051 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |