| About |
|---|
| SABIC® HDPE B5429 is a medium molecular weight high density polyethylene copolymer. It is typically used for blow moulding bottles of small sizes. SABIC® HDPE B5429 offers a very good combination of toughness, stress cracking resistance (ESCR), load bearing strength and processability characteristics. Typical applications. SABIC® HDPE B5429 is classified as a multipurpose blow moulding grade. It may be blow moulded into containers for household and industrial chemicals (e.g. detergents, bleach, fabric softeners, solvents, paints, etc.), automotive supplies, foodstuffs, toiletries and cosmetics. It is typically also used for other hollow thin-walled parts and profile extrusions. This product is not intended for and must not be used in any pharmaceutical/medical applications.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | HDPE copolymer |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good flexibility,Copolymer,High density,High ESCR |
| Availabilitys | Europe |
| Process Methods | Profile extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.954 | g/cm³ | ISO 1183 |
| Melt Flow Rate | ISO 1133 | ||
| 190℃，2.16kg | 0.30 | g/10min | ISO 1133 |
| 190℃，21.6kg | 29 | g/10min | ISO 1133 |
| 190℃，5.0kg | 1.5 | g/10min | ISO 1133 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| 10% non-ionic detergent, molded, F50 | 40.0 | hr | ASTM D1693B |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ISO 180/A | ||
| -30 ℃, molded | 5.0 | kJ/m² | ISO 180-A |
| 23 ℃, molded | 12 | kJ/m² | ISO 180-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 81.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | 127 | ℃ | ASTM D1525 2 |
| Melting temperature | 132 | ℃ | DIN 53765 |
| Enthalpy Change | 205 | J/g | DIN 53765 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Blow Molding Melt Temperature | 165 to 215 | ℃ |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D, molded | 61 | ISO 868 | |
| Tensile modulus | |||
| 2 mm, molded into shape | 1050 | MPa | ISO 527-2/1BA/50 |
| tensile strength | ISO 527-2/1BA/50 | ||
| Yield, 2 mm, molded | 26.0 | MPa | ISO 527-2/1BA/50 |
| Fracture, 2 mm, molded | 28.0 | MPa | ISO 527-2/1BA/50 |
| Tensile strain | |||
| Fracture, 2 mm, molded | > 1000 | % | ISO 527-2/1BA/50 |
| Bending modulus | |||
| 2 mm, molded into shape | 1250 | MPa | ISO 178 |
| bending strength | |||
| 2 mm, molded into shape | 27.0 | MPa | ISO 178 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |