Solanyl® C8105

About
Solanyl® C8105 is an end compound suitable for film applications and is specially developed for packaging. Solanyl® C8105 is starch free. Solanyl® C8105 can be processed on conventional blown or cast film extrusion lines suitable for (multi-layer) flexible films. Applications in which Solanyl® C8105 can be used are: T-shirt bags & waste bags&&

Product Description
Generic	生物可降解聚合物
Material Status	Commercial: Active
Features	Good flexibility,Renewable resources,Biodegradable
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.47	g/cm³	ISO 1183
Melt Flow Rate
190℃，2.16kg	2.0 to 4.5	g/10min	ISO 1133

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	405	MPa	ISO 527-2
tensile strength	16.0	MPa	ISO 527-2
Bending modulus	390	MPa	ISO 178
bending strength
3.50% strain	10.0	MPa	ISO 178

film	Nominal value	Unit	Test method
film thickness
test	20	µm
Tensile modulus
MD，20 µm	530	MPa
TD，20 µm	465	MPa
tensile strength
MD, fracture, 20 µ m	29.0	MPa
TD, fracture, 20 µ m	21.0	MPa
MD，20 µm	30.0	MPa
TD，20 µm	22.0	MPa
Tensile strain
fracture	370	%	ISO 527-2
MD, fracture, 20 µ m	280	%
TD, fracture, 20 µ m	400	%

THERMAL	Nominal value	Unit	Test method
Melting temperature
DSC	> 155	℃	ISO 3146

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.