| QR Resin QR-4004是一种聚苯醚 + 尼龙 66（PPE+尼龙 66）产品,。 它,在北美洲有供货。 主要特性为:耐化学品。&& |
| Product Description | |
|---|---|
| Generic | PPO(PPE)+PA 66 |
| Material Status | Commercial: Active |
| Features | Sprayable,Solvent resistance |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.08 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 280℃，2.16kg | 4.0 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.2 mm | 1.0 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 55.2 | MPa | ASTM D638 |
| Bending modulus | 2070 | MPa | ASTM D790 |
| bending strength | |||
| yield | 86.2 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 190 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed | 143 | ℃ | |
| 1.8 MPa, unannealed | 124 | ℃ |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 93.3 to 107 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Drying time, maximum | 6.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Barrel rear temperature | 249 to 277 | °C | |
| Barrel middle temperature | 254 to 282 | °C | |
| Barrel front temperature | 260 to 288 | °C | |
| Nozzle temperature | 271 to 293 | °C | |
| Processing (melt) temperature | 266 to 288 | °C | |
| Mold temperature | 65.6 to 93.3 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |