Amodel® LF-1930 HS

About
Amodel® LF-1930 HS is a 30% Long Glass Fiber reinforced, heat stabilized polyphtalamide PPA, with high heat deflection temperature, very high flexural modulus and low moisture absorption. It displays an excellent retention of properties in a wide temperature range as well as outstanding creep and fatigue resistance. Amodel® LF-1930 HS has a pellet length of 9mm and can be processed on most injection-molding machines. Black: Amodel® LF-1930 HS BK545 Natural: Amodel® LF-1930 HS NT&&

About

Amodel® LF-1930 HS is a 30% Long Glass Fiber reinforced, heat stabilized polyphtalamide PPA, with high heat deflection temperature, very high flexural modulus and low moisture absorption. It displays an excellent retention of properties in a wide temperature range as well as outstanding creep and fatigue resistance. Amodel® LF-1930 HS has a pellet length of 9mm and can be processed on most injection-molding machines. Black: Amodel® LF-1930 HS BK545 Natural: Amodel® LF-1930 HS NT&&

Product Description
Supplier	Solvay
Generic	PPA
Material Status	Commercial: Active
Features	Good Rigidity,Low CLTE,Low warping,Good flexibility,High impact resistance,Low contractility,Fatigue resistance,Insulation
Availabilitys	Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.44	g/cm³

MECHANICAL	Nominal value	Unit
Tensile modulus
23℃	11000	MPa
90℃	10000	MPa
120℃	6500	MPa
tensile strength
Fracture, 23 ℃	180	MPa
Fracture, 90 ℃	160	MPa
Fracture, 120 ℃	110	MPa
Tensile strain
fracture	1.8	%
Bending modulus
23℃	10300	MPa
bending strength
23℃	275	MPa

IMPACT	Nominal value	Unit
Charpy Notched Impact Strength
23℃	20	kJ/m²
Charpy Unnotch Impact strength
23℃	50	kJ/m²

THERMAL	Nominal value	Unit
Hot deformation temperature
0.45 MPa, unannealed	300	℃
1.8 MPa, unannealed	285	℃

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	120	°C
Drying time	4.0	hr
Recommended maximum moisture content	0.060	%
Proposed maximum recycled material ratio	20	%
Barrel rear temperature	325 to 340	°C
Barrel middle temperature	325 to 340	°C
Barrel front temperature	325 to 340	°C
Nozzle temperature	325 to 345	°C
Processing (melt) temperature	< 345	°C
Mold temperature	130 to 165	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.