| About |
|---|
| Flexible, non-halogenated FR, mPPE extrusion grade material for evaluation in automotive wire coating applications requiring ISO6722.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+SEBS+Polyolefin |
| Material Status | Commercial: Active |
| Features | Good flexibility,Halogen free,Flame Characteristics |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.03 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 280℃，5.0kg | 33 | g/10min | ASTM D1238 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| -30℃ | 170 | J/m | ASTM D256 |
| 23℃ | 560 | J/m | ASTM D256 |
| -30℃ | 14 | kJ/m² | ISO 180-1A |
| 23℃ | 37 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 3.2 mm | 82.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 3.2 mm | 56.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 64 mm span | 66.0 | ℃ | ISO 75-2/Af |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric constant | |||
| 1.00 GHz | 2.47 | ASTM D150 | |
| Dissipation factor | |||
| 1 GHz | 3.2E-3 | ASTM D150 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 10 seconds | 63 | ASTM D2240 | |
| Tensile modulus | |||
| — | 840 | MPa | ASTM D638 |
| — | 690 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 28.0 | MPa | ASTM D638 |
| yield | 25.0 | MPa | ISO 527-2 |
| fracture | 28.0 | MPa | ASTM D638 |
| fracture | 25.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 20 | % | ISO 527-2/50 |
| fracture | 90 | % | ASTM D638 |
| fracture | 50 | % | ISO 527-2/50 |
| Bending modulus | |||
| 50 mm span | 720 | MPa | ASTM D790 |
| — | 790 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 80.0 to 100 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Barrel 1 zone temperature | 200 to 260 | °C | |
| Barrel 3 zone temperature | 270 to 300 | °C | |
| Barrel 5 zone temperature | 280 to 300 | °C | |
| Melt temperature | 280 to 300 | °C | |
| Nozzle temperature | 280 to 300 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. Type I, 2.0 in/min |
| 4. 0.051 in/min |
| 5. 80*10*4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |