| KE101 is Outstanding impact strength and Excellent clarity PEN-PET copolyester Grade.&& |
| Product Description | |
|---|---|
| Supplier | Kolon |
| Generic | PEN+PET |
| Material Status | Commercial: Active |
| Features | Good Clarity,High impact resistance,V-2 |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.33 | g/cm³ | ASTM D792 |
| Density | 1.33 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 275℃，2.16kg | 15 | g/10min | ISO 1133 |
| 260℃，1.05kg | 8.1 | g/10min | ASTM D1238 |
| Shrinkage rate | 0.60 | % | ISO 294-4 |
| MD | 0.40 to 0.60 | % | ASTM D955 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 60% RH | 0.070 | % | ASTM D570 |
| 23℃，24hr | 0.10 | % | ISO 62 |
| Intrinsic viscosity | 0.88 | dl/g | Internal Method |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 3.5 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 77.0 | ℃ | ASTM D648-A |
| 0.45 MPa, unannealed | 75.0 | ℃ | ISO 75-2/B |
| Melting temperature | 230 | ℃ | ISO 11357-3 |
| Melting temperature | 234 | ℃ | ASTM D1525 |
| Linear coefficient of thermal expansion | |||
| MD | 6.0E-5 | 1/℃ | ASTM D696 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.80 mm | V-2 | UL 94 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Transmittance | |||
| total | 85.0 | % | ASTM D1003 |
| Haze | 1.5 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, 23 ℃ | 60.0 | MPa | ISO 527-2 |
| 23℃ | 60.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃ | 300 | % | ISO 527-2 |
| Fracture, 23 ℃ | 460 | % | ASTM D638 |
| Bending modulus | |||
| 23℃ | 2850 | MPa | ASTM D790 |
| 23℃ | 2900 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 92.0 | MPa | ASTM D790 |
| Rockwell hardness | 88 | ISO 2039-2 | |
| R-level | 88 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature – hot air dryer | 140 to 160 | °C | |
| Drying time – hot air dryer | 3.0 to 6.0 | hr | |
| Recommended maximum moisture content | < 0.080 | % | |
| Barrel rear temperature | 160 to 210 | °C | |
| Barrel middle temperature | 200 to 240 | °C | |
| Barrel front temperature | 220 to 250 | °C | |
| Nozzle temperature | 230 to 265 | °C | |
| Mold temperature | 30 to 80 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |